Ca0.12 Cu La1.88 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006182 _database_code_amcsd 0015091 CELL PARAMETERS: 5.3304 5.3663 13.1464 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 376.047 Density (g/cm3): 6.952 MAX. ABS. INTENSITY / VOLUME**2: 171.0925904 RIR: 8.013 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.47 4.37 6.5732 0 0 2 2 24.49 17.72 3.6344 1 1 1 8 27.13 10.43 3.2866 0 0 4 2 31.24 100.00 2.8630 1 1 3 8 33.39 32.20 2.6832 0 2 0 2 33.63 32.02 2.6652 2 0 0 2 41.20 10.87 2.1911 0 0 6 2 41.85 21.41 2.1588 1 1 5 8 43.54 11.27 2.0785 0 2 4 4 43.73 11.17 2.0701 2 0 4 4 48.12 29.33 1.8909 2 2 0 4 54.03 4.95 1.6971 0 2 6 4 54.19 4.98 1.6925 2 0 6 4 54.56 8.51 1.6821 1 1 7 8 54.56 1.65 1.6819 1 3 1 8 54.88 1.58 1.6730 3 1 1 8 55.96 4.17 1.6433 0 0 8 2 56.12 4.62 1.6390 2 2 4 8 58.35 14.53 1.5815 1 3 3 8 58.65 13.98 1.5742 3 1 3 8 65.17 8.23 1.4315 2 2 6 8 65.50 4.23 1.4251 1 3 5 8 65.78 4.30 1.4197 3 1 5 8 66.75 2.92 1.4014 0 2 8 4 66.89 2.87 1.3988 2 0 8 4 70.15 3.58 1.3416 0 4 0 2 70.69 3.61 1.3326 4 0 0 2 75.54 2.61 1.2586 1 3 7 8 75.81 2.60 1.2549 3 1 7 8 76.86 5.41 1.2404 2 2 8 8 79.04 5.05 1.2115 3 3 3 8 80.08 3.35 1.1983 2 4 0 4 80.47 3.40 1.1935 4 2 0 4 84.72 1.56 1.1441 0 4 6 4 85.14 6.50 1.1396 1 1 11 8 85.24 1.60 1.1386 4 0 6 4 85.41 1.68 1.1367 3 3 5 8 86.43 1.91 1.1258 2 4 4 8 86.82 1.91 1.1218 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.