Ca0.03 Cu La1.97 O4.12 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006188 _database_code_amcsd 0015097 CELL PARAMETERS: 5.3299 5.3870 13.1614 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 377.892 Density (g/cm3): 7.105 MAX. ABS. INTENSITY / VOLUME**2: 181.1402976 RIR: 8.301 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.46 3.28 6.5807 0 0 2 2 24.45 18.97 3.6410 1 1 1 8 27.10 10.54 3.2903 0 0 4 2 31.19 100.00 2.8675 1 1 3 8 33.26 31.43 2.6935 0 2 0 2 33.63 30.91 2.6649 2 0 0 2 41.15 10.61 2.1936 0 0 6 2 41.78 20.34 2.1618 1 1 5 8 43.42 11.56 2.0842 0 2 4 4 43.71 11.33 2.0709 2 0 4 4 48.03 28.76 1.8944 2 2 0 4 53.90 4.93 1.7009 0 2 6 4 54.15 4.93 1.6936 2 0 6 4 54.36 1.83 1.6876 1 3 1 8 54.48 8.81 1.6842 1 1 7 8 54.86 1.71 1.6735 3 1 1 8 55.89 4.07 1.6452 0 0 8 2 56.01 4.71 1.6418 2 2 4 8 58.15 14.90 1.5865 1 3 3 8 58.62 14.11 1.5748 3 1 3 8 65.05 7.99 1.4337 2 2 6 8 65.29 3.97 1.4291 1 3 5 8 65.74 4.01 1.4205 3 1 5 8 66.61 2.88 1.4040 0 2 8 4 66.83 2.81 1.3999 2 0 8 4 69.84 3.52 1.3468 0 4 0 2 70.70 3.49 1.3325 4 0 0 2 75.33 2.72 1.2617 1 3 7 8 75.75 2.68 1.2558 3 1 7 8 76.72 5.38 1.2422 2 2 8 8 78.87 5.16 1.2137 3 3 3 8 79.79 3.26 1.2020 2 4 0 4 80.40 3.27 1.1943 4 2 0 4 84.40 1.51 1.1477 0 4 6 4 85.01 6.37 1.1410 1 1 11 8 85.21 1.53 1.1388 4 0 6 4 85.23 1.56 1.1387 3 3 5 8 86.13 1.98 1.1290 2 4 4 8 86.74 1.95 1.1227 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.