Ca0.05 Cu La1.95 O4.1 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006189 _database_code_amcsd 0015098 CELL PARAMETERS: 5.3310 5.3826 13.1623 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 377.687 Density (g/cm3): 7.069 MAX. ABS. INTENSITY / VOLUME**2: 179.2626663 RIR: 8.257 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.45 3.41 6.5812 0 0 2 2 24.45 18.55 3.6400 1 1 1 8 27.10 10.45 3.2906 0 0 4 2 31.20 100.00 2.8671 1 1 3 8 33.29 31.44 2.6913 0 2 0 2 33.62 31.09 2.6655 2 0 0 2 41.15 10.74 2.1937 0 0 6 2 41.79 20.23 2.1617 1 1 5 8 43.44 11.48 2.0833 0 2 4 4 43.70 11.28 2.0712 2 0 4 4 48.04 28.80 1.8938 2 2 0 4 53.92 4.99 1.7004 0 2 6 4 54.15 5.02 1.6938 2 0 6 4 54.40 1.79 1.6865 1 3 1 8 54.48 8.72 1.6842 1 1 7 8 54.85 1.67 1.6737 3 1 1 8 55.88 4.07 1.6453 0 0 8 2 56.03 4.66 1.6414 2 2 4 8 58.18 14.85 1.5856 1 3 3 8 58.61 14.07 1.5750 3 1 3 8 65.06 8.09 1.4335 2 2 6 8 65.33 3.96 1.4284 1 3 5 8 65.73 4.01 1.4206 3 1 5 8 66.62 2.85 1.4038 0 2 8 4 66.82 2.77 1.4001 2 0 8 4 69.90 3.53 1.3456 0 4 0 2 70.68 3.51 1.3327 4 0 0 2 75.36 2.69 1.2612 1 3 7 8 75.74 2.66 1.2559 3 1 7 8 76.73 5.36 1.2420 2 2 8 8 78.90 5.13 1.2133 3 3 3 8 79.85 3.28 1.2013 2 4 0 4 80.40 3.30 1.1943 4 2 0 4 84.46 1.53 1.1470 0 4 6 4 85.01 6.37 1.1410 1 1 11 8 85.19 1.56 1.1390 4 0 6 4 85.25 1.57 1.1384 3 3 5 8 86.19 1.96 1.1284 2 4 4 8 86.74 1.94 1.1227 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.