Ca0.1 Cu La1.9 O4.05 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006191 _database_code_amcsd 0015100 CELL PARAMETERS: 5.3311 5.3653 13.1570 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 376.329 Density (g/cm3): 6.993 MAX. ABS. INTENSITY / VOLUME**2: 174.4075918 RIR: 8.121 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.46 3.70 6.5785 0 0 2 2 24.49 17.78 3.6345 1 1 1 8 27.11 10.28 3.2892 0 0 4 2 31.23 100.00 2.8640 1 1 3 8 33.40 31.57 2.6827 0 2 0 2 33.62 31.58 2.6655 2 0 0 2 41.17 10.91 2.1928 0 0 6 2 41.82 20.64 2.1600 1 1 5 8 43.53 11.16 2.0789 0 2 4 4 43.71 11.07 2.0709 2 0 4 4 48.12 28.90 1.8908 2 2 0 4 54.01 5.00 1.6978 0 2 6 4 54.16 5.06 1.6934 2 0 6 4 54.52 8.61 1.6831 1 1 7 8 54.57 1.68 1.6817 1 3 1 8 54.87 1.59 1.6732 3 1 1 8 55.91 4.05 1.6446 0 0 8 2 56.10 4.55 1.6393 2 2 4 8 58.35 14.65 1.5815 1 3 3 8 58.63 14.02 1.5745 3 1 3 8 65.14 8.21 1.4320 2 2 6 8 65.49 4.01 1.4253 1 3 5 8 65.75 4.12 1.4201 3 1 5 8 66.71 2.86 1.4021 0 2 8 4 66.84 2.79 1.3997 2 0 8 4 70.16 3.50 1.3413 0 4 0 2 70.68 3.56 1.3328 4 0 0 2 75.52 2.62 1.2590 1 3 7 8 75.77 2.63 1.2554 3 1 7 8 76.82 5.30 1.2409 2 2 8 8 79.04 5.08 1.2115 3 3 3 8 80.09 3.27 1.1982 2 4 0 4 80.46 3.34 1.1936 4 2 0 4 84.71 1.55 1.1442 0 4 6 4 85.06 6.41 1.1404 1 1 11 8 85.20 1.60 1.1389 4 0 6 4 85.39 1.59 1.1368 3 3 5 8 86.43 1.89 1.1258 2 4 4 8 86.80 1.89 1.1220 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.