As7 Mn6 Ni16 Lambert-Andron B, Chaudouet P, Madar R, Fruchart R Physica Status Solidi 82 (1984) K133-K136 Determination de la structure cristallographique de la phase de type G Ni16 Mn6 As7 _cod_database_code 1008985 _database_code_amcsd 0016848 CELL PARAMETERS: 11.4000 11.4000 11.4000 90.000 90.000 90.000 SPACE GROUP: Fm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1481.544 Density (g/cm3): 8.038 MAX. ABS. INTENSITY / VOLUME**2: 161.6290514 RIR: 6.547 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.45 8.57 6.5818 1 1 1 8 15.55 9.17 5.7000 2 0 0 6 25.92 1.96 3.4372 3 1 1 24 27.10 7.77 3.2909 2 2 2 8 34.29 2.95 2.6153 3 3 1 24 38.69 15.37 2.3270 4 2 2 24 41.14 28.38 2.1939 3 3 3 8 41.14 23.97 2.1939 5 1 1 24 44.98 100.00 2.0153 4 4 0 12 47.17 22.09 1.9270 5 3 1 48 47.88 7.48 1.9000 6 0 0 6 47.88 2.03 1.9000 4 4 2 24 50.64 5.05 1.8025 6 2 0 24 52.65 3.62 1.7385 5 3 3 24 53.30 19.37 1.7186 6 2 2 24 62.59 4.50 1.4842 7 3 1 48 65.50 6.84 1.4250 8 0 0 6 70.03 3.73 1.3435 8 2 2 24 70.03 5.52 1.3435 6 6 0 12 71.70 2.60 1.3164 5 5 5 8 71.70 1.84 1.3164 7 5 1 48 72.25 2.68 1.3077 6 6 2 24 74.44 1.17 1.2746 8 4 0 24 76.06 2.86 1.2513 9 1 1 24 76.06 5.54 1.2513 7 5 3 48 76.60 4.15 1.2438 8 4 2 48 78.75 1.16 1.2152 6 6 4 24 80.35 3.41 1.1950 9 3 1 48 82.99 11.77 1.1635 8 4 4 24 84.58 11.63 1.1457 9 3 3 24 85.10 1.69 1.1400 8 6 0 24 88.78 1.28 1.1021 9 5 1 48 88.78 1.94 1.1021 7 7 3 24 89.30 2.34 1.0970 10 2 2 24 89.30 5.74 1.0970 6 6 6 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.