Co3 O8 U2 Bacmann M, Lambert-Andron B Physica Status Solidi A72 (1982) 833-837 Structures cristallines de Co3 U2 O8 a 300 K et 110 K _cod_database_code 1008902 _database_code_amcsd 0016769 CELL PARAMETERS: 5.1100 10.3000 6.1500 90.000 90.000 90.000 SPACE GROUP: Pnnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 323.693 Density (g/cm3): 8.010 MAX. ABS. INTENSITY / VOLUME**2: 273.0624215 RIR: 11.100 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.22 20.23 5.1500 0 2 0 2 22.62 49.91 3.9303 1 0 1 4 24.24 4.94 3.6721 1 1 1 8 28.57 100.00 3.1244 1 2 1 8 29.04 14.44 3.0750 0 0 2 2 29.80 8.21 2.9978 0 3 1 4 31.39 8.65 2.8498 1 3 0 4 33.95 24.74 2.6402 0 2 2 4 34.69 1.39 2.5857 1 3 1 8 34.84 13.89 2.5750 0 4 0 2 35.12 13.63 2.5550 2 0 0 2 35.16 11.21 2.5526 1 1 2 8 36.22 1.70 2.4798 2 1 0 4 38.38 3.35 2.3456 1 2 2 8 39.37 3.56 2.2888 2 2 0 4 41.94 12.71 2.1539 1 4 1 8 44.19 2.15 2.0497 2 3 0 4 45.97 5.46 1.9742 0 4 2 4 46.19 6.58 1.9652 2 0 2 4 46.49 2.26 1.9533 0 5 1 4 46.71 4.30 1.9446 2 3 1 8 47.08 2.56 1.9303 2 1 2 8 47.59 2.19 1.9106 1 5 0 4 47.81 7.81 1.9026 1 0 3 4 49.65 20.04 1.8360 2 2 2 8 50.31 14.68 1.8137 2 4 0 4 51.18 14.88 1.7847 1 2 3 8 51.95 2.52 1.7601 0 3 3 4 53.75 2.05 1.7055 2 3 2 8 56.02 2.30 1.6415 3 0 1 4 56.72 10.74 1.6228 1 5 2 8 56.79 2.75 1.6211 3 1 1 8 58.69 7.02 1.5732 1 6 1 8 59.06 8.53 1.5640 3 2 1 8 59.14 3.94 1.5622 2 4 2 8 59.58 1.75 1.5518 2 5 1 8 60.19 5.53 1.5375 0 0 4 2 60.50 4.93 1.5302 1 4 3 8 61.90 4.32 1.4989 0 6 2 4 62.74 2.04 1.4810 3 3 1 8 63.04 2.71 1.4747 3 1 2 8 63.10 1.15 1.4732 0 2 4 4 64.26 1.87 1.4495 2 3 3 8 65.19 2.57 1.4310 0 7 1 4 66.08 2.26 1.4140 1 7 0 4 67.69 1.88 1.3842 3 4 1 8 69.46 1.25 1.3531 1 3 4 8 71.46 2.84 1.3201 0 4 4 4 71.63 2.90 1.3174 2 0 4 4 72.09 1.22 1.3101 3 0 3 4 72.77 1.27 1.2996 3 1 3 8 73.21 1.65 1.2929 2 6 2 8 74.24 1.56 1.2775 4 0 0 2 74.44 2.41 1.2745 1 6 3 8 74.77 3.02 1.2697 3 2 3 8 74.90 1.24 1.2678 4 1 0 4 76.26 2.46 1.2485 2 7 1 8 79.37 2.26 1.2073 3 5 2 8 80.32 1.47 1.1954 0 7 3 4 81.05 1.68 1.1864 3 6 1 8 82.19 5.05 1.1728 2 4 4 8 82.26 1.36 1.1721 4 1 2 8 82.63 1.34 1.1677 3 4 3 8 82.88 4.02 1.1649 1 2 5 8 84.19 1.65 1.1500 4 2 2 8 84.21 1.08 1.1498 2 8 0 4 84.70 1.21 1.1444 4 4 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.