Lead
      Davey W P
      Physical Review 25 (1925) 753-761
      Lattice constants of twelve common metals
      Locality: synthetic
      Note: lattice parameter is average of runs 1 & 2
      _database_code_amcsd 0015134

      CELL PARAMETERS:    4.9200   4.9200   4.9200   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    119.095
      Density (g/cm3):     11.554
      MAX. ABS. INTENSITY / VOLUME**2:      1023.061129    
      RIR:     28.831
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                31.49        100.00        2.8406    1   1   1         8
                36.53         49.41        2.4600    2   0   0         6
                52.62         31.53        1.7395    2   2   0        12
                62.62         34.49        1.4834    3   1   1        24
                65.75          9.68        1.4203    2   2   2         8
                77.62          4.08        1.2300    4   0   0         6
                86.16         11.78        1.1287    3   3   1        24
                88.97         10.78        1.1001    4   2   0        24
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.