Javorieite Gurewitz E, Majovsky J, Shaked H Physical Review B9 (1974) 1071-1078 Neutron-diffraction study of the magnetic structure of KFeCl3 Locality: Synthetic _database_code_amcsd 0020628 CELL PARAMETERS: 8.7150 3.8450 14.1500 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 474.155 Density (g/cm3): 2.820 MAX. ABS. INTENSITY / VOLUME**2: 13.74998357 RIR: 1.588 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.93 39.61 7.4205 1 0 1 4 12.51 31.87 7.0750 0 0 2 2 16.14 44.92 5.4928 1 0 2 4 20.38 3.33 4.3575 2 0 0 2 21.34 14.19 4.1645 2 0 1 4 21.42 10.69 4.1481 1 0 3 4 23.98 6.44 3.7102 2 0 2 4 25.17 4.57 3.5375 0 0 4 2 26.10 26.01 3.4139 1 1 1 8 27.21 3.81 3.2778 1 0 4 4 27.87 10.90 3.2007 2 0 3 4 29.98 2.53 2.9802 0 1 3 4 31.02 19.45 2.8831 2 1 0 4 31.67 100.00 2.8250 2 1 1 8 31.73 29.62 2.8199 1 1 3 8 32.60 18.12 2.7464 2 0 4 4 33.29 51.21 2.6916 1 0 5 4 33.34 15.93 2.6873 3 0 2 4 33.57 96.97 2.6699 2 1 2 8 36.01 6.58 2.4944 1 1 4 8 36.53 6.28 2.4599 2 1 3 8 37.91 8.08 2.3734 2 0 5 4 39.39 2.26 2.2874 3 1 1 8 39.54 18.37 2.2792 0 1 5 4 39.59 9.51 2.2765 1 0 6 4 40.17 8.72 2.2450 3 0 4 4 40.36 2.23 2.2349 2 1 4 8 40.97 10.82 2.2026 3 1 2 8 41.96 1.21 2.1534 4 0 1 4 43.46 6.55 2.0823 4 0 2 4 44.88 3.56 2.0196 2 1 5 8 45.88 17.75 1.9779 4 0 3 4 46.10 2.11 1.9692 1 0 7 4 46.35 12.03 1.9589 1 1 6 8 46.86 37.04 1.9387 3 1 4 8 47.28 33.56 1.9225 0 2 0 2 47.99 10.80 1.8956 4 1 0 4 48.94 1.89 1.8611 1 2 1 8 49.11 1.74 1.8552 0 2 2 4 49.11 1.06 1.8551 4 0 4 4 49.72 5.76 1.8337 2 0 7 4 49.80 7.12 1.8310 4 1 2 8 49.80 3.03 1.8309 3 0 6 4 49.96 2.82 1.8254 2 1 6 8 50.28 3.72 1.8146 1 2 2 8 51.05 4.55 1.7892 0 1 7 4 51.68 4.53 1.7687 0 0 8 2 51.99 12.60 1.7589 4 1 3 8 52.19 28.28 1.7527 1 1 7 8 52.42 1.89 1.7455 2 2 1 8 52.46 1.40 1.7443 1 2 3 8 53.05 5.56 1.7264 4 0 5 4 53.70 1.13 1.7070 2 2 2 8 54.20 4.37 1.6924 5 0 2 4 54.96 3.98 1.6708 4 1 4 8 55.37 4.18 1.6593 3 0 7 4 55.41 1.10 1.6583 1 2 4 8 55.52 2.27 1.6551 2 1 7 8 55.78 2.70 1.6481 2 2 3 8 58.40 1.44 1.5802 1 1 8 8 58.61 4.70 1.5750 2 2 4 8 58.61 1.70 1.5749 4 1 5 8 59.05 13.54 1.5644 1 2 5 8 59.08 4.15 1.5636 3 2 2 8 59.08 1.89 1.5635 5 0 4 4 61.37 1.07 1.5108 3 0 8 4 61.65 3.93 1.5046 5 1 3 8 62.14 3.12 1.4939 2 2 5 8 62.59 2.77 1.4841 5 0 5 4 62.90 1.27 1.4775 4 1 6 8 63.32 3.82 1.4688 1 2 6 8 63.73 3.11 1.4603 3 2 4 8 64.11 1.51 1.4525 6 0 0 2 64.32 1.54 1.4483 5 1 4 8 64.97 4.27 1.4354 1 1 9 8 65.62 7.11 1.4228 6 0 2 4 66.02 1.34 1.4150 0 0 10 2 66.16 2.91 1.4125 4 2 2 8 67.67 5.31 1.3845 5 1 5 8 67.77 6.65 1.3827 3 0 9 4 67.91 5.19 1.3803 2 1 9 8 68.00 8.52 1.3786 4 2 3 8 68.17 1.11 1.3756 1 2 7 8 70.58 2.53 1.3344 6 1 2 8 71.04 3.06 1.3269 2 2 7 8 71.10 1.57 1.3259 3 2 6 8 71.92 1.12 1.3128 1 1 10 8 72.38 1.48 1.3057 6 1 3 8 72.63 2.52 1.3017 0 2 8 4 73.19 1.54 1.2932 4 1 8 8 73.76 3.33 1.2845 4 2 5 8 74.73 2.63 1.2703 5 2 2 8 75.72 2.68 1.2561 3 2 7 8 78.00 4.19 1.2250 2 3 1 8 78.01 1.91 1.2249 6 1 5 8 78.03 1.16 1.2245 1 3 3 8 78.92 1.47 1.2130 5 2 4 8 79.04 4.92 1.2114 2 3 2 8 79.33 1.26 1.2077 3 1 10 8 81.03 1.39 1.1867 4 0 10 4 81.90 1.56 1.1762 3 0 11 4 82.03 2.28 1.1748 5 2 5 8 82.03 1.05 1.1747 2 1 11 8 82.56 1.15 1.1685 1 0 12 4 82.65 1.40 1.1675 0 3 5 4 83.40 1.27 1.1589 6 2 0 4 84.76 6.04 1.1437 6 2 2 8 85.14 1.18 1.1396 0 2 10 4 86.26 1.95 1.1277 6 1 7 8 86.75 5.98 1.1225 3 2 9 8 87.28 3.60 1.1171 5 1 9 8 87.30 1.23 1.1168 1 3 6 8 87.68 4.15 1.1131 3 3 4 8 88.51 1.19 1.1047 4 3 0 4 89.75 2.11 1.0926 7 1 5 8 89.87 1.08 1.0915 4 3 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.