Barioperovskite Shirane G, Danner H, Pepinsky R Physical Review 105 (1957) 856-860 Neutron diffraction study of orthorhombic BaTiO3 Locality: synthetic Note: orthorhombic structure _database_code_amcsd 0018581 CELL PARAMETERS: 3.9900 5.6690 5.6820 90.000 90.000 90.000 SPACE GROUP: Amm2 X-RAY WAVELENGTH: 1.541838 Cell Volume: 128.523 Density (g/cm3): 6.025 MAX. ABS. INTENSITY / VOLUME**2: 139.1740479 RIR: 7.522 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.15 19.45 4.0132 0 1 1 2 22.28 9.55 3.9900 1 0 0 2 31.49 25.34 2.8410 0 0 2 1 31.56 25.12 2.8345 0 2 0 2 31.62 100.00 2.8295 1 1 1 4 38.92 18.05 2.3143 1 0 2 2 38.98 17.81 2.3108 1 2 0 4 45.19 32.31 2.0066 0 2 2 2 45.46 15.95 1.9950 2 0 0 2 50.83 2.07 1.7964 0 1 3 2 50.93 1.99 1.7931 0 3 1 2 50.94 4.03 1.7927 1 2 2 4 51.13 3.91 1.7864 2 1 1 4 56.15 16.21 1.6380 1 1 3 4 56.24 16.15 1.6355 1 3 1 4 56.35 8.05 1.6327 2 0 2 2 56.40 8.02 1.6314 2 2 0 4 65.74 3.96 1.4205 0 0 4 1 65.91 4.04 1.4173 0 4 0 2 66.04 15.93 1.4148 2 2 2 4 70.55 1.38 1.3350 2 1 3 4 70.63 1.33 1.3336 2 3 1 4 74.75 2.97 1.2700 0 2 4 2 74.86 5.90 1.2683 1 3 3 4 74.87 2.94 1.2682 0 4 2 2 75.27 5.77 1.2625 3 1 1 4 79.14 2.70 1.2101 1 2 4 4 79.26 2.62 1.2086 1 4 2 4 79.59 1.29 1.2045 3 0 2 2 79.62 1.28 1.2040 3 2 0 4 83.55 3.35 1.1571 2 0 4 2 83.71 3.42 1.1554 2 4 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.