Fe Nd Si2 Malaman B, Venturini G, Le Caer G, Pontonnier L, Fruchart D, Tomala K, Sanchez J Physical Review B41 (1990) 4700-4712 Magnetic structures of PrFeSi2 and NdFeSi2 from neutron and Mossbauer studies _cod_database_code 1008442 _database_code_amcsd 0016347 CELL PARAMETERS: 4.0820 16.9800 4.0040 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 277.527 Density (g/cm3): 6.132 MAX. ABS. INTENSITY / VOLUME**2: 144.2899975 RIR: 7.662 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.42 2.03 8.4900 0 2 0 2 20.93 5.86 4.2450 0 4 0 2 22.40 19.77 3.9689 1 1 0 4 24.58 28.67 3.6215 0 2 1 4 26.93 5.40 3.3108 1 3 0 4 30.69 11.98 2.9127 0 4 1 4 31.62 14.39 2.8300 0 6 0 2 31.74 10.78 2.8188 1 1 1 8 34.35 35.60 2.6107 1 5 0 4 35.17 100.00 2.5515 1 3 1 8 38.97 17.16 2.3110 0 6 1 4 41.28 6.01 2.1869 1 5 1 8 42.60 2.43 2.1225 0 8 0 2 44.38 19.45 2.0410 2 0 0 2 45.30 18.21 2.0020 0 0 2 2 48.55 11.13 1.8753 0 8 1 4 49.56 1.03 1.8394 2 4 0 4 51.10 3.68 1.7875 1 1 2 8 51.39 6.49 1.7781 2 2 1 8 53.49 1.33 1.7131 1 3 2 8 53.51 9.61 1.7126 1 9 0 4 54.93 3.83 1.6715 2 4 1 8 55.51 4.76 1.6554 2 6 0 4 56.29 4.52 1.6344 0 6 2 4 58.06 13.01 1.5887 1 5 2 8 58.63 5.83 1.5746 1 9 1 8 60.52 7.98 1.5298 2 6 1 8 63.20 1.18 1.4712 2 8 0 4 63.92 1.13 1.4564 0 8 2 4 64.54 1.08 1.4438 1 11 0 4 65.29 10.35 1.4292 2 0 2 4 67.87 6.96 1.3809 2 8 1 8 69.16 6.67 1.3582 1 11 1 8 70.60 1.70 1.3341 0 12 1 4 72.65 6.57 1.3014 1 9 2 8 74.35 3.21 1.2758 2 6 2 8 75.23 2.61 1.2631 3 5 0 4 75.72 7.52 1.2562 3 3 1 8 77.04 7.09 1.2379 1 3 3 8 78.93 2.44 1.2129 0 14 0 2 79.38 1.57 1.2072 0 6 3 4 80.92 1.21 1.1880 1 13 1 8 86.05 1.61 1.1299 0 8 3 4 87.31 1.64 1.1167 2 12 1 8 88.62 1.77 1.1036 3 9 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.