Fe Nd Si2 Malaman B, Venturini G, Le Caer G, Pontonnier L, Fruchart D, Tomala K, Sanchez J Physical Review B41 (1990) 4700-4712 Magnetic structures of PrFeSi2 and NdFeSi2 from neutron and Mossbauer studies _cod_database_code 1008443 _database_code_amcsd 0016348 CELL PARAMETERS: 4.0720 16.8960 3.9960 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 274.927 Density (g/cm3): 6.190 MAX. ABS. INTENSITY / VOLUME**2: 142.0058156 RIR: 7.470 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.47 2.99 8.4480 0 2 0 2 21.03 5.59 4.2240 0 4 0 2 22.46 20.04 3.9587 1 1 0 4 24.65 31.40 3.6123 0 2 1 4 27.02 5.40 3.2998 1 3 0 4 30.80 10.78 2.9029 0 4 1 4 31.78 14.75 2.8160 0 6 0 2 31.82 11.43 2.8123 1 1 1 8 34.49 39.19 2.6004 1 5 0 4 35.27 100.00 2.5444 1 3 1 8 39.13 17.92 2.3019 0 6 1 4 41.43 6.19 2.1795 1 5 1 8 42.82 2.58 2.1120 0 8 0 2 44.50 19.97 2.0360 2 0 0 2 45.39 18.72 1.9980 0 0 2 2 48.77 11.22 1.8672 0 8 1 4 51.22 3.72 1.7837 1 1 2 8 51.53 7.08 1.7737 2 2 1 8 53.62 1.33 1.7091 1 3 2 8 53.77 8.74 1.7049 1 9 0 4 55.10 3.45 1.6669 2 4 1 8 55.71 4.89 1.6499 2 6 0 4 56.47 4.65 1.6295 0 6 2 4 58.23 14.34 1.5843 1 5 2 8 58.89 6.10 1.5681 1 9 1 8 60.73 8.35 1.5250 2 6 1 8 63.46 1.25 1.4658 2 8 0 4 64.17 1.20 1.4514 0 8 2 4 64.88 1.19 1.4372 1 11 0 4 65.45 10.63 1.4260 2 0 2 4 68.14 7.00 1.3761 2 8 1 8 69.51 7.95 1.3524 1 11 1 8 70.97 1.33 1.3280 0 12 1 4 71.74 1.02 1.3157 0 2 3 4 72.94 5.99 1.2969 1 9 2 8 74.60 3.31 1.2722 2 6 2 8 75.48 2.88 1.2595 3 5 0 4 75.94 7.49 1.2530 3 3 1 8 77.24 7.07 1.2352 1 3 3 8 79.40 2.56 1.2069 0 14 0 2 79.62 1.66 1.2041 0 6 3 4 82.72 1.01 1.1667 1 11 2 8 86.35 1.62 1.1266 0 8 3 4 87.75 1.27 1.1123 2 12 1 8 88.99 1.62 1.0999 3 9 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.