Fe Nd Si2 Malaman B, Venturini G, Le Caer G, Pontonnier L, Fruchart D, Tomala K, Sanchez J Physical Review B41 (1990) 4700-4712 Magnetic structures of PrFeSi2 and NdFeSi2 from neutron and Mossbauer studies _cod_database_code 1008444 _database_code_amcsd 0016349 CELL PARAMETERS: 4.0720 16.8960 3.9960 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 274.927 Density (g/cm3): 6.190 MAX. ABS. INTENSITY / VOLUME**2: 139.1363818 RIR: 7.319 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.47 3.37 8.4480 0 2 0 2 21.03 5.60 4.2240 0 4 0 2 22.46 20.10 3.9587 1 1 0 4 24.65 33.00 3.6123 0 2 1 4 27.02 6.24 3.2998 1 3 0 4 30.80 10.64 2.9029 0 4 1 4 31.78 13.69 2.8160 0 6 0 2 31.82 11.68 2.8123 1 1 1 8 34.49 41.06 2.6004 1 5 0 4 35.27 100.00 2.5444 1 3 1 8 39.13 18.89 2.3019 0 6 1 4 41.43 7.24 2.1795 1 5 1 8 42.82 3.21 2.1120 0 8 0 2 44.50 20.38 2.0360 2 0 0 2 45.39 19.11 1.9980 0 0 2 2 48.77 11.30 1.8672 0 8 1 4 51.22 3.73 1.7837 1 1 2 8 51.53 7.44 1.7737 2 2 1 8 53.62 1.54 1.7091 1 3 2 8 53.77 8.70 1.7049 1 9 0 4 55.10 3.40 1.6669 2 4 1 8 55.71 4.52 1.6499 2 6 0 4 56.47 4.31 1.6295 0 6 2 4 58.23 15.04 1.5843 1 5 2 8 58.89 5.35 1.5681 1 9 1 8 60.73 8.80 1.5250 2 6 1 8 63.46 1.57 1.4658 2 8 0 4 64.17 1.51 1.4514 0 8 2 4 65.45 10.84 1.4260 2 0 2 4 68.14 7.05 1.3761 2 8 1 8 69.51 9.08 1.3524 1 11 1 8 70.97 1.18 1.3280 0 12 1 4 71.74 1.07 1.3157 0 2 3 4 72.94 5.94 1.2969 1 9 2 8 74.60 3.05 1.2722 2 6 2 8 75.48 3.03 1.2595 3 5 0 4 75.94 7.48 1.2530 3 3 1 8 77.24 7.06 1.2352 1 3 3 8 79.40 2.69 1.2069 0 14 0 2 79.62 1.74 1.2041 0 6 3 4 81.36 1.01 1.1827 1 13 1 8 81.43 1.25 1.1819 2 8 2 8 86.35 1.63 1.1266 0 8 3 4 87.75 1.12 1.1123 2 12 1 8 88.47 1.04 1.1051 2 2 3 8 88.99 1.60 1.0999 3 9 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.