Marshite Hull S, Keen D A Physical Review B50 (1994) 5868-5885 High-pressure polymorphism of the copper(I) halides: A neutron-diffraction study to ~10 GPa Note: P = 5.55 GPa Note: known as CuI-V _database_code_amcsd 0015183 CELL PARAMETERS: 4.0229 4.0229 5.6506 90.000 90.000 90.000 SPACE GROUP: P4/nmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 91.448 Density (g/cm3): 6.916 MAX. ABS. INTENSITY / VOLUME**2: 238.1994665 RIR: 11.215 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.68 8.77 5.6506 0 0 1 2 27.21 100.00 3.2772 1 0 1 8 31.45 7.45 2.8446 1 1 0 4 31.67 1.84 2.8253 0 0 2 2 35.33 33.37 2.5408 1 1 1 8 38.95 9.63 2.3121 1 0 2 8 45.07 29.51 2.0115 2 0 0 4 45.24 48.75 2.0046 1 1 2 8 48.01 1.52 1.8950 2 0 1 8 48.32 7.63 1.8835 0 0 3 2 53.45 27.26 1.7143 2 1 1 16 53.74 7.27 1.7058 1 0 3 8 56.13 1.57 1.6386 2 0 2 8 61.06 4.63 1.5175 2 1 2 16 65.64 8.25 1.4223 2 2 0 4 66.15 1.80 1.4126 0 0 4 2 68.21 9.23 1.3749 2 0 3 8 70.68 4.31 1.3329 1 0 4 8 72.44 5.02 1.3047 3 0 1 8 72.68 5.39 1.3010 2 1 3 16 74.60 1.36 1.2722 3 1 0 8 76.80 4.70 1.2411 3 1 1 16 79.04 1.01 1.2114 3 0 2 8 83.30 12.40 1.1600 3 1 2 16 83.65 3.24 1.1560 2 0 4 8 85.56 4.38 1.1350 2 2 3 8 87.87 4.58 1.1111 2 1 4 16 89.54 5.52 1.0946 3 2 1 16 89.77 1.49 1.0924 3 0 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.