Nantokite Hull S, Keen D A Physical Review B50 (1994) 5868-5885 High-pressure polymorphism of the copper(I) halides: A neutron-diffraction study to ~10 GPa Note: P = 0 GPa Note: ZnS structure, sphalerite structure Note: known as CuCl-II _database_code_amcsd 0015185 CELL PARAMETERS: 5.4202 5.4202 5.4202 90.000 90.000 90.000 SPACE GROUP: F-43m X-RAY WAVELENGTH: 1.541838 Cell Volume: 159.238 Density (g/cm3): 4.129 MAX. ABS. INTENSITY / VOLUME**2: 105.9449518 RIR: 8.355 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 28.52 100.00 3.1294 1 1 1 4 33.05 7.95 2.7101 2 0 0 6 47.44 49.39 1.9163 2 2 0 12 56.29 27.07 1.6343 3 1 1 12 59.04 1.21 1.5647 2 2 2 4 69.35 5.03 1.3550 4 0 0 6 76.63 6.94 1.2435 3 3 1 12 88.34 7.34 1.1064 4 2 2 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.