CuBr
      Hull S, Keen D A
      Physical Review B50 (1994) 5868-5885
      High-pressure polymorphism of the copper(I) halides:
      A neutron-diffraction study to ~10 GPa
      Note: P = 0 GPa
      Note: ZnS structure, sphalerite structure
      Note: known as CuBr-III
      _database_code_amcsd 0015189

      CELL PARAMETERS:    5.6955   5.6955   5.6955   90.000   90.000   90.000
      SPACE GROUP: F-43m     
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    184.755
      Density (g/cm3):      5.156
      MAX. ABS. INTENSITY / VOLUME**2:      174.8939536    
      RIR:     11.044
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                27.12        100.00        3.2883    1   1   1         4
                31.41          1.01        2.8477    2   0   0         6
                45.02         60.89        2.0137    2   2   0        12
                53.35         33.27        1.7173    3   1   1        12
                65.56          7.20        1.4239    4   0   0         6
                72.31         10.03        1.3066    3   3   1        12
                83.07         11.19        1.1626    4   2   2        12
                89.39          1.53        1.0961    3   3   3         4
                89.39          4.59        1.0961    5   1   1        12
================================================================================