Nd Ni O3 Garcia-Munoz J, Rodriguez-Carvajal, Lacorre P, Torrance J Physical Review B46 (1992) 4414-4425 Neutron-diffraction study of RNiO3 (R= La, Pr, Nd, Sm): Electronically induced structural changes across the metal-insulator transition _cod_database_code 1000317 _database_code_amcsd 0015266 CELL PARAMETERS: 5.3879 5.3797 7.6058 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 220.456 Density (g/cm3): 7.559 MAX. ABS. INTENSITY / VOLUME**2: 221.3977452 RIR: 9.537 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.37 11.89 3.8069 1 1 0 4 23.39 6.73 3.8029 0 0 2 2 26.18 5.22 3.4043 1 1 1 8 33.26 25.33 2.6939 2 0 0 2 33.30 100.00 2.6905 1 1 2 8 33.31 22.99 2.6899 0 2 0 2 35.40 3.82 2.5359 0 2 1 4 41.06 9.24 2.1983 2 0 2 4 41.10 7.95 2.1960 0 2 2 4 42.86 1.84 2.1102 1 1 3 8 47.78 24.11 1.9035 2 2 0 4 47.84 13.53 1.9015 0 0 4 2 49.35 3.32 1.8465 2 2 1 8 49.40 1.92 1.8449 0 2 3 4 53.81 1.22 1.7035 3 1 0 4 53.86 1.41 1.7021 2 2 2 8 53.90 2.09 1.7011 1 1 4 8 55.33 4.75 1.6604 1 3 1 8 59.45 18.19 1.5547 3 1 2 8 59.51 8.82 1.5535 2 0 4 4 59.52 12.24 1.5531 1 3 2 8 59.54 8.00 1.5527 0 2 4 4 60.86 1.16 1.5222 2 2 3 8 66.14 2.25 1.4128 1 3 3 8 69.83 2.93 1.3470 4 0 0 2 69.93 11.09 1.3452 2 2 4 8 69.95 2.02 1.3449 0 4 0 2 71.20 1.42 1.3244 0 4 1 4 76.04 1.32 1.2517 3 3 1 8 79.60 2.45 1.2044 4 2 0 4 79.65 4.19 1.2037 3 3 2 8 79.68 1.68 1.2033 2 4 0 4 79.73 5.71 1.2027 1 1 6 8 80.88 1.60 1.1885 2 4 1 8 85.59 1.14 1.1348 3 3 3 8 85.66 1.08 1.1340 1 3 5 8 89.08 2.49 1.0991 4 0 4 4 89.19 1.67 1.0980 0 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.