Bixbyite-(Mn) Cockayne E, Levin I, Wu H, Llobet A Physical Review B87 (2013) 184413 Magnetic structure of bixbyite alpha-Mn2O3: A combined DFT+U and neutron diffraction study Note: T = 2 K Locality: synthetic _database_code_amcsd 0021110 CELL PARAMETERS: 9.4078 9.4488 9.3739 90.000 90.000 90.000 SPACE GROUP: Pbca X-RAY WAVELENGTH: 1.541838 Cell Volume: 833.269 Density (g/cm3): 5.033 MAX. ABS. INTENSITY / VOLUME**2: 83.38060624 RIR: 5.394 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.06 1.25 4.2189 0 2 1 4 23.10 4.19 3.8495 1 2 1 8 23.16 5.52 3.8412 2 1 1 8 23.20 4.66 3.8342 1 1 2 8 28.50 1.60 3.1324 2 1 2 8 32.97 100.00 2.7164 2 2 2 8 38.10 6.35 2.3622 0 4 0 2 38.27 6.10 2.3519 4 0 0 2 38.41 5.98 2.3435 0 0 4 2 45.15 3.62 2.0080 3 3 2 8 45.19 3.73 2.0063 2 3 3 8 45.24 2.63 2.0044 3 2 3 8 49.26 1.76 1.8497 3 4 1 8 49.32 1.82 1.8476 1 4 3 8 49.32 2.15 1.8475 4 3 1 8 49.43 1.92 1.8437 1 3 4 8 49.45 2.50 1.8430 4 1 3 8 49.50 1.39 1.8412 3 1 4 8 55.10 11.29 1.6667 4 4 0 4 55.21 13.46 1.6637 0 4 4 4 55.34 11.05 1.6601 4 0 4 4 60.68 1.33 1.5262 6 1 1 8 60.90 1.01 1.5211 1 1 6 8 63.98 1.63 1.4553 4 5 1 8 64.07 1.14 1.4534 1 5 4 8 64.25 1.17 1.4498 5 1 4 8 64.30 1.61 1.4487 4 1 5 8 65.61 7.53 1.4229 2 6 2 8 65.85 5.69 1.4184 6 2 2 8 66.04 7.15 1.4146 2 2 6 8 67.47 1.01 1.3882 6 3 1 8 67.74 1.33 1.3833 3 1 6 8 69.17 3.61 1.3582 4 4 4 8 81.49 1.02 1.1811 0 8 0 2 82.28 1.01 1.1717 0 0 8 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.