Stetindite-(Ce) Skakle J M S, Dickson C L, Glasser F P Powder Diffraction 15 (2000) 234-238 The crystal structures of CeSiO4 and Ca2Ce8(SiO4)6O2 Locality: synthetic _database_code_amcsd 0015318 CELL PARAMETERS: 6.9564 6.9564 6.1953 90.000 90.000 90.000 SPACE GROUP: I4_1/amd X-RAY WAVELENGTH: 1.541838 Cell Volume: 299.800 Density (g/cm3): 5.144 MAX. ABS. INTENSITY / VOLUME**2: 112.4014222 RIR: 7.115 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.18 64.97 4.6265 1 0 1 8 25.61 100.00 3.4782 2 0 0 4 32.20 21.33 2.7802 2 1 1 16 34.21 62.77 2.6212 1 1 2 8 36.53 18.03 2.4595 2 2 0 4 38.93 3.49 2.3133 2 0 2 8 41.59 21.92 2.1717 3 0 1 8 45.84 14.50 1.9797 1 0 3 8 49.48 18.44 1.8421 3 2 1 16 50.91 51.72 1.7936 3 1 2 16 52.63 13.47 1.7391 4 0 0 4 53.24 7.37 1.7205 2 1 3 16 56.53 5.27 1.6279 4 1 1 16 59.42 10.44 1.5555 4 2 0 8 59.70 2.83 1.5488 0 0 4 2 59.99 3.66 1.5422 3 0 3 8 64.28 14.82 1.4491 3 3 2 8 66.03 9.46 1.4149 2 0 4 8 66.30 1.96 1.4098 3 2 3 16 69.21 6.20 1.3575 4 3 1 16 69.21 1.45 1.3575 5 0 1 8 72.06 8.11 1.3106 2 2 4 8 72.32 3.57 1.3066 4 1 3 16 75.13 1.58 1.2646 5 2 1 16 76.26 9.89 1.2485 5 1 2 16 77.64 2.61 1.2297 4 4 0 4 83.35 3.70 1.1594 6 0 0 4 83.60 4.43 1.1566 4 0 4 8 83.85 2.03 1.1538 5 0 3 8 83.85 1.47 1.1538 4 3 3 16 84.09 3.03 1.1511 2 1 5 16 86.55 1.95 1.1246 6 1 1 16 87.65 8.58 1.1133 5 3 2 16 89.00 4.29 1.0999 6 2 0 8 89.24 8.51 1.0975 4 2 4 16 89.49 1.88 1.0952 5 2 3 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.