TiNi Sitepu H Powder Diffraction 24 (2009) 315-326 Texture and structural refinement using neutron diffraction data from molybdite (MoO3) and calcite (CaCO3) powders and a Ni-rich Ni50.7Ti49.30 alloy Note: Aged Locality: synthetic _database_code_amcsd 0018901 CELL PARAMETERS: 2.8894 4.1334 4.6321 90.000 90.000 96.929 SPACE GROUP: P2_1/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 54.917 Density (g/cm3): 6.443 MAX. ABS. INTENSITY / VOLUME**2: 210.4212417 RIR: 10.634 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.66 2.40 4.1032 0 1 0 2 29.07 100.00 3.0715 0 1 1 4 31.18 1.61 2.8683 1 0 0 2 35.97 3.05 2.4965 -1 1 0 2 38.88 25.31 2.3161 0 0 2 2 40.49 3.67 2.2280 1 1 0 2 44.14 8.53 2.0516 0 2 0 2 45.16 2.01 2.0078 1 1 1 4 48.53 1.61 1.8758 0 2 1 4 54.01 1.74 1.6979 1 -1 2 4 55.50 5.65 1.6558 -1 2 1 4 57.39 2.26 1.6057 1 1 2 4 60.26 5.86 1.5357 0 2 2 4 62.03 5.47 1.4961 1 2 1 4 64.48 7.87 1.4451 0 1 3 4 65.03 3.06 1.4341 2 0 0 2 66.41 1.82 1.4078 -2 1 0 2 68.49 2.09 1.3700 2 0 1 4 69.83 3.71 1.3469 2 -1 1 4 72.95 1.77 1.2968 -1 3 0 2 75.68 3.29 1.2567 2 1 1 4 78.43 3.21 1.2193 2 0 2 4 79.53 2.11 1.2053 2 -2 1 4 79.71 1.95 1.2030 2 -1 2 4 81.55 1.79 1.1805 1 3 0 2 82.92 1.45 1.1644 -1 2 3 4 83.47 1.93 1.1580 0 0 4 2 85.89 2.12 1.1315 -1 3 2 4 88.52 1.68 1.1046 1 2 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.