Fe4O5 Lavina B, Dera P, Kim E, Meng Y, Downs R T, Weck P F, Sutton S R, Zhao Y Proceedings of the National Academy of Sciences 108 (2011) 17281-17284 Discovery of the recoverable high-pressure iron oxide Fe4O5 Locality: synthetic Note: P = 10 GPa _database_code_amcsd 0018509 CELL PARAMETERS: 2.8430 9.7000 12.2900 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 338.923 Density (g/cm3): 5.945 MAX. ABS. INTENSITY / VOLUME**2: 50.05400070 RIR: 2.742 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.41 4.92 6.1450 0 0 2 2 23.37 2.17 3.8071 0 2 2 4 28.52 1.51 3.1296 0 2 3 4 33.65 23.33 2.6634 1 1 1 8 34.56 100.00 2.5955 0 2 4 4 36.02 28.72 2.4935 1 1 2 8 37.07 27.18 2.4250 0 4 0 2 39.69 11.35 2.2708 1 1 3 8 41.17 9.42 2.1925 0 2 5 4 42.33 1.53 2.1350 1 3 0 4 43.00 26.99 2.1035 1 3 1 8 44.22 1.70 2.0483 0 0 6 2 44.95 49.53 2.0168 1 3 2 8 48.05 23.19 1.8933 1 3 3 8 48.23 3.50 1.8869 0 2 6 4 49.94 2.63 1.8262 1 1 5 8 52.17 1.07 1.7533 1 3 4 8 56.15 16.06 1.6380 1 1 6 8 57.15 2.47 1.6119 1 3 5 8 57.51 1.01 1.6025 1 5 0 4 58.05 1.71 1.5890 1 5 1 8 59.63 10.59 1.5506 1 5 2 8 60.24 8.38 1.5362 0 0 8 2 61.68 1.43 1.5038 0 6 3 4 62.21 9.92 1.4924 1 5 3 8 62.87 7.14 1.4781 1 3 6 8 62.95 10.98 1.4764 1 1 7 8 65.21 16.34 1.4307 0 6 4 4 65.68 10.86 1.4215 2 0 0 2 65.72 2.28 1.4208 1 5 4 8 69.29 3.97 1.3561 1 3 7 8 72.89 7.10 1.2978 0 4 8 4 75.30 3.57 1.2621 1 5 6 8 76.39 11.61 1.2468 2 2 4 8 77.90 4.03 1.2263 2 4 0 4 78.32 2.37 1.2208 1 7 2 8 78.96 2.87 1.2125 0 8 0 2 80.61 1.02 1.1918 1 7 3 8 86.94 1.68 1.1206 1 1 10 8 89.37 1.07 1.0963 0 4 10 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.