Celestine James R Proceedings of the Royal Society of London A109 (1925) 598-620 The Crystal Structures of Barytes, Celestine and Anglesite _cod_database_code 1010543 _database_code_amcsd 0017448 CELL PARAMETERS: 8.3600 5.3600 6.8400 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 306.498 Density (g/cm3): 2.593 MAX. ABS. INTENSITY / VOLUME**2: 23.69367376 RIR: 2.975 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.75 2.81 5.2939 1 0 1 4 21.06 38.28 4.2189 0 1 1 4 21.26 8.99 4.1800 2 0 0 2 23.62 49.00 3.7665 1 1 1 8 24.97 19.55 3.5667 2 0 1 4 26.05 28.50 3.4200 0 0 2 2 27.05 100.00 3.2962 2 1 0 4 28.19 67.38 3.1654 1 0 2 4 30.10 91.46 2.9694 2 1 1 8 32.86 41.39 2.7256 1 1 2 8 33.44 49.50 2.6800 0 2 0 2 34.76 15.37 2.5807 3 0 1 4 37.91 20.09 2.3733 2 1 2 8 38.73 3.72 2.3252 3 1 1 8 39.96 3.69 2.2561 2 2 0 4 42.18 9.49 2.1426 2 2 1 8 42.87 12.68 2.1095 0 2 2 4 43.12 1.99 2.0981 0 1 3 4 44.28 34.85 2.0454 1 2 2 8 44.52 26.53 2.0350 1 1 3 8 45.26 23.55 2.0037 3 1 2 8 45.37 27.68 1.9988 4 0 1 4 46.65 6.95 1.9472 4 1 0 4 48.62 1.59 1.8728 4 1 1 8 49.00 10.24 1.8589 3 2 1 8 51.81 15.98 1.7646 3 0 3 4 52.97 3.02 1.7287 0 3 1 4 53.59 1.71 1.7100 0 0 4 2 54.18 4.12 1.6929 1 3 1 8 54.77 5.47 1.6761 3 1 3 8 54.80 7.38 1.6753 1 0 4 4 55.97 10.05 1.6429 2 3 0 4 56.67 1.86 1.6242 5 0 1 4 57.52 24.15 1.6022 4 2 1 8 57.65 8.01 1.5990 1 1 4 8 57.71 10.97 1.5975 2 3 1 8 58.30 1.60 1.5827 2 0 4 4 59.40 5.76 1.5559 1 3 2 8 59.47 3.07 1.5544 5 1 1 8 61.05 2.67 1.5179 2 1 4 8 62.74 3.56 1.4809 2 3 2 8 63.08 15.74 1.4738 3 2 3 8 64.42 5.10 1.4464 5 1 2 8 64.66 1.72 1.4416 0 2 4 4 65.73 7.63 1.4206 1 2 4 8 66.48 3.66 1.4064 3 1 4 8 67.19 1.18 1.3933 6 0 0 2 67.42 1.98 1.3890 5 2 1 8 67.54 6.04 1.3868 1 3 3 8 68.10 5.48 1.3768 3 3 2 8 68.90 1.74 1.3628 2 2 4 8 69.17 1.67 1.3581 4 3 0 4 69.73 2.56 1.3485 6 1 0 4 69.75 3.22 1.3483 5 0 3 4 70.24 4.00 1.3400 0 4 0 2 71.13 3.12 1.3255 0 1 5 4 71.28 7.22 1.3230 6 1 1 8 72.25 6.49 1.3076 5 1 3 8 72.73 1.77 1.3001 2 0 5 4 73.74 3.18 1.2849 4 1 4 8 75.20 2.71 1.2635 2 1 5 8 75.76 1.75 1.2555 3 3 3 8 75.83 1.27 1.2545 6 1 2 8 75.84 1.17 1.2544 2 4 1 8 76.33 1.68 1.2476 0 4 2 4 77.16 1.42 1.2362 6 2 0 4 77.33 4.85 1.2340 1 4 2 8 78.22 2.76 1.2221 1 3 4 8 79.59 4.07 1.2045 5 2 3 8 79.80 1.09 1.2018 5 3 1 8 80.82 1.73 1.1892 3 4 1 8 82.45 2.31 1.1698 2 2 5 8 82.71 1.43 1.1668 5 1 4 8 84.21 1.99 1.1498 5 3 2 8 84.68 2.17 1.1446 4 0 5 4 85.10 1.51 1.1400 0 0 6 2 86.10 1.47 1.1294 3 3 4 8 86.27 2.32 1.1275 7 0 2 4 87.35 1.10 1.1164 3 2 5 8 87.68 5.77 1.1130 4 4 1 8 89.12 1.19 1.0987 6 3 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.