Ba Cu Nd2 O5 Michel C, Er-Rakho L, Raveau B Revue de Chimie Minerale 21 (1984) 85-91 Les oxides Nd2-x Ba1+x Cu1-x/2 O5-x _cod_database_code 1001327 _database_code_amcsd 0015396 CELL PARAMETERS: 6.6950 6.6950 5.8190 90.000 90.000 90.000 SPACE GROUP: P4/mbm X-RAY WAVELENGTH: 1.541838 Cell Volume: 260.825 Density (g/cm3): 7.248 MAX. ABS. INTENSITY / VOLUME**2: 166.0620986 RIR: 7.460 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.23 12.11 5.8190 0 0 1 2 24.24 16.65 3.6723 1 1 1 8 26.63 1.65 3.3475 2 0 0 4 29.84 22.13 2.9941 2 1 0 8 30.73 39.54 2.9095 0 0 2 2 30.82 100.00 2.9016 2 0 1 8 33.66 56.30 2.6623 2 1 1 16 36.24 1.10 2.4788 1 1 2 8 38.01 21.94 2.3670 2 2 0 4 41.10 1.29 2.1960 2 0 2 8 41.17 3.06 2.1926 2 2 1 8 42.71 18.09 2.1171 3 1 0 8 43.37 38.60 2.0866 2 1 2 16 45.60 3.89 1.9896 3 1 1 16 49.65 18.31 1.8361 2 2 2 8 50.87 1.98 1.7949 1 1 3 8 53.53 8.78 1.7119 3 1 2 16 54.69 16.77 1.6783 2 0 3 8 56.53 10.19 1.6279 2 1 3 16 56.69 6.36 1.6238 4 1 0 8 57.28 9.51 1.6085 4 0 1 8 58.49 3.16 1.5780 3 3 0 4 59.06 11.60 1.5640 4 1 1 16 60.82 9.78 1.5230 3 3 1 8 61.99 6.68 1.4970 4 2 0 8 64.00 5.96 1.4547 0 0 4 2 64.20 2.22 1.4508 4 0 2 8 64.24 2.68 1.4498 4 2 1 16 65.24 1.12 1.4302 3 1 3 16 65.87 8.18 1.4179 4 1 2 16 67.53 1.98 1.3871 3 3 2 8 70.78 7.76 1.3312 4 2 2 16 72.20 2.88 1.3085 2 1 4 16 74.01 1.64 1.2808 5 1 1 16 74.94 3.76 1.2672 4 0 3 8 76.51 4.55 1.2451 4 1 3 16 76.93 3.81 1.2394 2 2 4 8 78.07 4.09 1.2241 3 3 3 8 78.70 2.26 1.2158 5 2 1 16 80.03 3.64 1.1990 3 1 4 16 81.16 1.21 1.1851 4 2 3 16 81.29 1.48 1.1835 4 4 0 4 84.35 1.68 1.1482 5 3 0 8 84.80 2.67 1.1432 5 2 2 16 86.37 1.13 1.1265 5 3 1 16 87.40 3.37 1.1158 6 0 0 4 89.06 3.17 1.0993 2 0 5 8 89.37 1.04 1.0963 4 4 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.