Fe O3 Tb Bertaut E, Chappert J, Mareschal J, Rebouillat J, Sivardiere J Solid State Communications 5 (1967) 293-298 Structures magnetiques de Tb Fe O3 _cod_database_code 1008091 _database_code_amcsd 0016033 CELL PARAMETERS: 5.3260 5.6020 7.6350 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 227.800 Density (g/cm3): 7.661 MAX. ABS. INTENSITY / VOLUME**2: 211.0729894 RIR: 8.971 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.33 1.56 4.3682 1 0 1 4 23.04 19.20 3.8599 1 1 0 4 23.30 12.98 3.8175 0 0 2 2 25.86 21.43 3.4447 1 1 1 8 31.95 18.79 2.8010 0 2 0 2 33.00 100.00 2.7143 1 1 2 8 33.66 24.64 2.6630 2 0 0 2 34.10 13.06 2.6296 0 2 1 4 39.27 4.46 2.2940 2 1 1 8 39.92 5.14 2.2583 0 2 2 4 41.34 9.63 2.1841 2 0 2 4 42.55 7.53 2.1247 1 1 3 8 43.53 1.39 2.0791 1 2 2 8 47.09 16.17 1.9300 2 2 0 4 47.64 13.31 1.9088 0 0 4 2 48.32 6.89 1.8836 0 2 3 4 48.66 11.67 1.8711 2 2 1 8 52.34 1.15 1.7480 2 1 3 8 53.36 15.64 1.7170 1 3 1 8 53.56 3.33 1.7110 1 1 4 8 54.20 1.60 1.6924 3 1 0 4 55.63 2.34 1.6523 3 1 1 8 57.61 5.74 1.5999 1 3 2 8 58.52 6.81 1.5773 0 2 4 4 59.59 9.44 1.5514 2 0 4 4 59.77 18.24 1.5472 3 1 2 8 60.17 4.14 1.5378 2 2 3 8 64.30 7.38 1.4488 1 3 3 8 68.06 3.10 1.3775 0 4 1 4 69.23 7.02 1.3571 2 2 4 8 70.20 1.01 1.3407 0 2 5 4 70.76 2.09 1.3315 4 0 0 2 74.83 3.25 1.2688 3 3 1 8 75.00 1.16 1.2663 3 1 4 8 77.85 1.28 1.2270 0 4 3 4 78.11 3.36 1.2235 2 4 1 8 78.44 1.48 1.2193 3 3 2 8 79.27 5.83 1.2085 1 1 6 8 79.74 1.54 1.2025 4 2 0 4 80.15 2.25 1.1975 2 2 5 8 80.93 1.69 1.1879 4 2 1 8 83.83 3.22 1.1540 1 3 5 8 84.35 2.62 1.1482 3 3 3 8 87.54 3.06 1.1144 2 4 3 8 89.81 1.90 1.0920 4 0 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.