Cr7.87 Ga4.13 O19 Sr Obradors X, Labarta A, Isalgue A, Tejada J, Rodriguez J, Pernet M Solid State Communications 65 (1988) 189-192 Magnetic frustration and lattice dimensionality in Sr Cr8 Ga4 O19 _cod_database_code 1006009 _database_code_amcsd 0015456 CELL PARAMETERS: 5.7993 5.7993 22.6584 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 659.950 Density (g/cm3): 5.478 MAX. ABS. INTENSITY / VOLUME**2: 44.05239194 RIR: 2.618 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.80 2.88 11.3292 0 0 2 2 17.66 35.52 5.0223 1 0 0 6 18.09 12.65 4.9033 1 0 1 12 19.33 33.03 4.5914 1 0 2 12 21.24 19.40 4.1821 1 0 3 12 23.56 6.89 3.7764 0 0 6 2 23.68 18.05 3.7580 1 0 4 12 26.49 16.83 3.3645 1 0 5 12 29.60 36.41 3.0183 1 0 6 12 30.84 46.29 2.8997 1 1 0 6 31.59 12.04 2.8323 0 0 8 2 31.86 2.49 2.8091 1 1 2 12 32.92 50.40 2.7208 1 0 7 12 34.76 100.00 2.5811 1 1 4 12 35.98 24.50 2.4959 2 0 1 12 36.42 39.26 2.4670 1 0 8 12 36.65 25.94 2.4517 2 0 2 12 37.75 22.41 2.3829 2 0 3 12 39.17 4.82 2.2999 1 1 6 12 39.24 10.66 2.2957 2 0 4 12 40.06 1.38 2.2507 1 0 9 12 41.09 7.06 2.1965 2 0 5 12 43.27 1.73 2.0911 2 0 6 12 43.83 2.66 2.0654 1 0 10 12 45.73 3.77 1.9841 2 0 7 12 47.72 1.49 1.9058 1 0 11 12 47.92 4.55 1.8983 2 1 0 12 48.10 1.98 1.8916 2 1 1 24 48.45 7.88 1.8790 2 0 8 12 48.63 8.41 1.8722 2 1 2 24 49.51 1.38 1.8410 2 1 3 24 50.72 3.70 1.7999 2 1 4 24 51.16 2.15 1.7854 1 1 10 12 51.72 9.64 1.7674 1 0 12 12 52.25 3.57 1.7509 2 1 5 24 54.07 12.93 1.6960 2 1 6 24 54.55 13.17 1.6823 2 0 10 12 54.84 7.82 1.6741 3 0 0 6 56.17 21.03 1.6375 2 1 7 24 56.89 5.68 1.6185 0 0 14 2 57.39 20.13 1.6055 3 0 4 12 57.90 31.00 1.5926 2 0 11 12 58.32 1.25 1.5823 1 1 12 12 58.54 20.94 1.5769 2 1 8 24 60.49 1.12 1.5305 3 0 6 12 61.44 12.05 1.5092 2 0 12 12 63.98 1.08 1.4551 2 1 10 24 64.25 40.34 1.4498 2 2 0 6 65.15 6.42 1.4319 2 0 13 12 66.12 1.12 1.4132 1 1 14 12 67.05 1.03 1.3959 2 1 11 24 67.21 1.19 1.3929 3 1 0 12 67.78 1.88 1.3825 3 1 2 24 68.89 2.82 1.3630 1 0 16 12 69.04 3.35 1.3604 2 0 14 12 69.44 1.33 1.3535 2 2 6 12 69.49 1.13 1.3527 3 1 4 24 70.32 7.63 1.3387 2 1 12 24 70.76 1.35 1.3315 3 1 5 24 72.30 4.04 1.3069 3 1 6 24 73.36 4.77 1.2906 2 2 8 12 73.51 1.95 1.2883 1 0 17 12 74.10 7.44 1.2795 3 1 7 24 75.89 2.39 1.2537 4 0 1 12 76.16 6.51 1.2500 3 1 8 24 76.30 2.03 1.2479 4 0 2 12 76.99 2.25 1.2386 4 0 3 12 77.94 1.48 1.2258 4 0 4 12 83.77 5.93 1.1547 1 1 18 12 84.38 1.03 1.1479 4 0 8 12 85.56 2.81 1.1351 2 1 16 24 85.76 1.09 1.1329 0 0 20 2 86.90 3.32 1.1209 3 1 12 24 88.46 1.78 1.1052 1 0 20 12 89.17 2.43 1.0982 4 0 10 12 89.40 1.10 1.0960 4 1 0 12 89.94 1.70 1.0908 2 1 17 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.