Ba2 Cu3 O6.91 Y
      Francois M, Junod A, Yvon K, Hewat A, Capponi J, Strobel P, Marezio M, Fischer P
      Solid State Communications 66 (1988) 1117-1125
      A study of the Cu-O chains in the high Tc superconductor Y Ba2 Cu3 O7
      by high resolution neutron powder diffraction
      _cod_database_code 1008410
      _database_code_amcsd 0016319

      CELL PARAMETERS:    3.8148   3.8815  11.6681   90.000   90.000   90.000
      SPACE GROUP: Pmmm      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    172.771
      Density (g/cm3):      6.388
      MAX. ABS. INTENSITY / VOLUME**2:      2.976005663    
      RIR:      0.152
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                 7.58        100.00       11.6681    0   0   1         2
                15.19          5.19        5.8341    0   0   2         2
                22.91          2.02        3.8815    0   1   0         2
                32.59          6.25        2.7474    0   1   3         4
                32.89          5.86        2.7235    1   0   3         4
                32.92          5.54        2.7207    1   1   0         4
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.