Ce0.1 Cu Nd1.9 O4 Paulus E, Yehia I, Fuess H, Rodriguez J, Vogt T, Stroebel J, Klauda M, Saemann-Ischenko G Solid State Communications 73 (1990) 791-795 Crystal structure refinement of Nd2-xCexCuO4 (x=.05-.30) by x-ray (295K) and neutron (1.5K) powder diffraction _cod_database_code 1006016 _database_code_amcsd 0015471 CELL PARAMETERS: 3.9407 3.9407 12.0945 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 187.817 Density (g/cm3): 7.348 MAX. ABS. INTENSITY / VOLUME**2: 278.7224227 RIR: 12.351 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.75 18.93 3.7468 1 0 1 8 29.54 2.58 3.0236 0 0 4 2 31.75 100.00 2.8180 1 0 3 8 32.12 34.84 2.7865 1 1 0 4 43.92 2.80 2.0615 1 0 5 8 44.20 17.22 2.0491 1 1 4 8 44.97 6.27 2.0157 0 0 6 2 46.07 24.69 1.9704 2 0 0 4 52.47 3.51 1.7439 2 1 1 16 55.68 1.77 1.6508 2 0 4 8 56.33 11.60 1.6332 1 1 6 8 57.03 30.91 1.6148 2 1 3 16 58.31 5.26 1.5824 1 0 7 8 61.32 1.57 1.5118 0 0 8 2 65.53 1.41 1.4244 2 1 5 16 66.34 6.42 1.4090 2 0 6 8 67.19 6.24 1.3932 2 2 0 4 70.92 1.18 1.3288 1 1 8 8 74.62 2.22 1.2719 1 0 9 8 76.23 5.44 1.2489 3 0 3 8 76.43 4.41 1.2462 3 1 0 8 77.34 3.80 1.2338 2 1 7 16 79.99 2.33 1.1994 2 0 8 8 84.00 3.19 1.1521 3 1 4 16 84.54 2.79 1.1461 2 2 6 8 88.03 1.31 1.1095 1 1 10 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.