Ce0.3 Cu Nd1.7 O4 Paulus E, Yehia I, Fuess H, Rodriguez J, Vogt T, Stroebel J, Klauda M, Saemann-Ischenko G Solid State Communications 73 (1990) 791-795 Crystal structure refinement of Nd2-xCexCuO4 (x=.05-.30) by x-ray (295K) and neutron (1.5K) powder diffraction _cod_database_code 1006021 _database_code_amcsd 0015476 CELL PARAMETERS: 3.9429 3.9429 12.0288 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 187.003 Density (g/cm3): 7.365 MAX. ABS. INTENSITY / VOLUME**2: 274.5714416 RIR: 12.138 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.75 19.52 3.7467 1 0 1 8 29.71 2.70 3.0072 0 0 4 2 31.83 100.00 2.8113 1 0 3 8 32.10 35.38 2.7880 1 1 0 4 44.10 3.28 2.0537 1 0 5 8 44.30 17.76 2.0445 1 1 4 8 45.23 6.01 2.0048 0 0 6 2 46.04 25.16 1.9714 2 0 0 4 52.45 3.62 1.7447 2 1 1 16 55.76 1.86 1.6487 2 0 4 8 56.54 11.18 1.6277 1 1 6 8 57.06 31.07 1.6141 2 1 3 16 58.60 5.32 1.5753 1 0 7 8 61.69 1.70 1.5036 0 0 8 2 65.65 1.65 1.4222 2 1 5 16 66.52 6.20 1.4057 2 0 6 8 67.15 6.36 1.3940 2 2 0 4 71.26 1.36 1.3234 1 1 8 8 75.04 1.98 1.2658 1 0 9 8 76.23 5.48 1.2489 3 0 3 8 76.38 4.49 1.2468 3 1 0 8 77.57 3.88 1.2307 2 1 7 16 80.30 2.55 1.1956 2 0 8 8 84.03 3.32 1.1518 3 1 4 16 84.69 2.71 1.1445 2 2 6 8 88.53 1.27 1.1045 1 1 10 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.