Ba Ni O5 Tm2 Salinas-Sanchez A, Saez-Puche R, Rodriguez-Carvajal J, Martinez J Solid State Communications 78 (1991) 481-488 Structural characterization of R2BaNiO5 (R=Tm and Yb): polymorphism for R=Tm _cod_database_code 1006037 _database_code_amcsd 0015484 CELL PARAMETERS: 3.7513 5.7214 11.2456 90.000 90.000 90.000 SPACE GROUP: Immm X-RAY WAVELENGTH: 1.541838 Cell Volume: 241.360 Density (g/cm3): 8.446 MAX. ABS. INTENSITY / VOLUME**2: 291.7534773 RIR: 11.248 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.76 5.06 5.6228 0 0 2 2 17.39 3.37 5.0994 0 1 1 4 25.02 9.09 3.5585 1 0 1 4 28.45 8.13 3.1371 1 1 0 4 28.47 33.34 3.1355 0 1 3 4 31.27 31.27 2.8607 0 2 0 2 31.83 10.58 2.8114 0 0 4 2 32.69 100.00 2.7396 1 1 2 8 33.80 2.92 2.6516 1 0 3 4 40.46 11.67 2.2296 1 2 1 8 43.22 8.77 2.0932 0 1 5 4 45.22 13.62 2.0052 0 2 4 4 46.71 9.49 1.9447 1 2 3 8 47.11 13.49 1.9290 1 0 5 4 48.54 13.16 1.8756 2 0 0 2 48.58 3.69 1.8743 0 0 6 2 53.93 1.44 1.7000 1 3 0 4 53.94 4.45 1.6998 0 3 3 4 56.56 18.23 1.6273 1 3 2 8 57.23 7.88 1.6096 2 1 3 8 57.26 1.11 1.6090 1 1 6 8 57.63 13.40 1.5993 1 2 5 8 58.88 8.85 1.5686 2 2 0 4 58.91 1.90 1.5677 0 2 6 4 59.22 3.08 1.5603 2 0 4 4 59.79 4.09 1.5467 0 1 7 4 62.94 2.19 1.4768 1 0 7 4 64.01 2.27 1.4546 0 3 5 4 65.23 4.49 1.4303 0 4 0 2 66.99 3.85 1.3969 2 1 5 8 68.50 6.04 1.3698 2 2 4 8 71.11 1.80 1.3258 2 0 6 4 71.96 1.13 1.3122 1 2 7 8 73.88 5.73 1.2828 1 1 8 8 74.42 1.39 1.2748 0 4 4 4 75.48 2.72 1.2595 2 3 3 8 77.72 1.72 1.2287 0 3 7 4 79.72 1.35 1.2029 2 2 6 8 80.45 5.18 1.1937 3 1 2 8 80.49 2.87 1.1933 2 1 7 8 84.24 1.73 1.1494 2 3 5 8 84.29 3.49 1.1489 1 4 5 8 85.35 3.50 1.1374 2 4 0 4 86.55 1.16 1.1246 0 0 10 2 89.72 1.45 1.0929 3 0 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.