Ba0.15 Ca Cu2 La1.85 O6 Navarro J, Fuertes A, Gomez-Romero P, Rodriguez-Carjaval J Solid State Communications 81 (1992) 677-681 Crystal structure of La1.85 Ba0.15 Ca Cu2 O6+y determined by neutron powder diffraction _cod_database_code 1006110 _database_code_amcsd 0015487 CELL PARAMETERS: 3.8330 3.8330 19.5327 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 286.978 Density (g/cm3): 6.276 MAX. ABS. INTENSITY / VOLUME**2: 107.1805433 RIR: 5.561 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.17 10.40 4.8832 0 0 4 2 23.65 3.87 3.7613 1 0 1 8 26.99 31.77 3.3031 1 0 3 8 27.40 2.97 3.2555 0 0 6 2 32.73 100.00 2.7360 1 0 5 8 33.05 75.87 2.7104 1 1 0 4 34.34 4.53 2.6117 1 1 2 8 36.81 10.71 2.4416 0 0 8 2 39.96 28.01 2.2559 1 0 7 8 43.44 18.34 2.0830 1 1 6 8 46.49 3.69 1.9533 0 0 10 2 47.44 41.97 1.9165 2 0 0 4 48.18 8.58 1.8886 1 0 9 8 50.30 8.22 1.8141 1 1 8 8 51.20 2.24 1.7840 2 0 4 8 55.43 7.53 1.6577 2 1 3 16 55.65 1.50 1.6516 2 0 6 8 56.54 6.93 1.6277 0 0 12 2 57.17 3.29 1.6112 1 0 11 8 58.22 3.87 1.5846 1 1 10 8 58.83 30.98 1.5697 2 1 5 16 61.51 7.21 1.5076 2 0 8 8 63.72 10.88 1.4606 2 1 7 16 67.07 8.27 1.3954 1 1 12 8 68.60 3.41 1.3680 2 0 10 8 69.34 10.34 1.3552 2 2 0 4 69.93 4.53 1.3452 2 1 9 16 75.89 1.29 1.2538 3 0 3 8 76.83 9.03 1.2406 2 0 12 8 76.85 1.02 1.2405 1 1 14 8 77.38 2.20 1.2333 2 1 11 16 78.81 5.55 1.2144 3 0 5 8 78.99 8.49 1.2121 3 1 0 8 81.18 2.62 1.1849 2 2 8 8 83.15 2.10 1.1617 3 0 7 8 85.48 2.89 1.1359 3 1 6 16 87.64 1.44 1.1134 2 2 10 8 88.88 1.03 1.1010 3 0 9 8 88.93 7.04 1.1006 1 0 17 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.