Ba0.6 Bi0.4 F2.4 Soubeyroux J, Reau J, Wahbi M, Senegas, Soo S Solid State Communications 82 (1992) 63-70 Neutron diffraction investigation of the Ba1-xBixF2-x solid solution _cod_database_code 1008593 _database_code_amcsd 0016484 CELL PARAMETERS: 6.0377 6.0377 6.0377 90.000 90.000 90.000 SPACE GROUP: Fm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 220.097 Density (g/cm3): 6.385 MAX. ABS. INTENSITY / VOLUME**2: 287.9413979 RIR: 14.685 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 25.55 100.00 3.4859 1 1 1 8 29.59 42.70 3.0189 2 0 0 6 42.34 55.72 2.1346 2 2 0 12 50.11 48.56 1.8204 3 1 1 24 52.50 9.81 1.7429 2 2 2 8 61.43 7.30 1.5094 4 0 0 6 67.64 16.68 1.3851 3 3 1 24 69.64 10.35 1.3501 4 2 0 24 77.44 13.40 1.2324 4 2 2 24 83.13 8.33 1.1620 5 1 1 24 83.13 2.43 1.1620 3 3 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.