Bi1.72 O3 Sr0.53 Boivin J, Thomas D Solid State Ionics 3 (1981) 457-462 Structural investigations on bismuth-based oxides _cod_database_code 1004071 _database_code_amcsd 0015498 CELL PARAMETERS: 3.9710 3.9710 28.4100 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 387.973 Density (g/cm3): 7.773 MAX. ABS. INTENSITY / VOLUME**2: 237.2355032 RIR: 9.938 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.34 5.84 9.4700 0 0 3 2 18.74 8.88 4.7350 0 0 6 2 26.10 29.94 3.4141 1 0 1 6 26.67 52.28 3.3424 0 1 2 6 28.27 53.60 3.1567 0 0 9 2 28.84 100.00 3.0952 1 0 4 6 30.38 56.81 2.9421 0 1 5 6 34.17 17.68 2.6237 1 0 7 6 36.37 13.11 2.4705 0 1 8 6 41.22 8.41 2.1903 1 0 10 6 43.84 9.89 2.0652 0 1 11 6 45.69 48.82 1.9855 1 1 0 6 48.04 1.52 1.8940 0 0 15 2 49.41 24.58 1.8445 1 0 13 6 49.80 3.48 1.8310 1 1 6 12 52.35 13.46 1.7477 0 1 14 6 53.38 3.43 1.7164 0 2 1 6 53.69 6.55 1.7070 2 0 2 6 54.61 44.10 1.6807 1 1 9 12 54.94 14.39 1.6712 0 2 4 6 55.86 9.47 1.6458 2 0 5 6 58.28 3.48 1.5833 0 2 7 6 58.48 5.48 1.5783 0 0 18 2 58.50 4.24 1.5777 1 0 16 6 59.75 2.68 1.5476 2 0 8 6 61.71 4.02 1.5031 0 1 17 6 63.21 1.80 1.4710 0 2 10 6 65.18 2.75 1.4313 2 0 11 6 68.46 2.51 1.3705 1 1 15 12 69.57 7.46 1.3513 0 2 13 6 71.91 1.76 1.3129 0 1 20 6 71.98 4.42 1.3119 2 0 14 6 72.84 2.24 1.2985 2 1 1 12 73.11 4.44 1.2944 1 2 2 12 74.16 10.10 1.2786 2 1 4 12 74.95 7.02 1.2671 1 2 5 12 77.04 2.70 1.2379 2 1 7 12 77.21 12.45 1.2355 1 1 18 12 77.23 1.58 1.2352 0 2 16 6 78.33 2.09 1.2206 1 2 8 12 79.24 4.79 1.2089 1 0 22 6 80.07 1.60 1.1984 2 0 17 6 81.42 1.41 1.1820 2 1 10 12 83.08 2.31 1.1625 0 1 23 6 83.21 2.46 1.1611 1 2 11 12 84.52 5.76 1.1463 3 0 0 6 87.27 7.11 1.1171 2 1 13 12 89.55 4.43 1.0945 1 2 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.