Ba0.156 Bi0.844 O1.422 Conflant P, Boivin J, Nowogrocki G, Thomas D Solid State Ionics 9 (1983) 925-928 Etude structurale par diffractometrie x a haute temperature du conducteur anionique Bi.844 Ba.156 O1.422 _cod_database_code 1004079 _database_code_amcsd 0015504 CELL PARAMETERS: 4.0570 4.0570 28.9000 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 411.944 Density (g/cm3): 2.667 MAX. ABS. INTENSITY / VOLUME**2: 38.73254056 RIR: 4.729 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.18 22.58 9.6333 0 0 3 2 18.42 12.36 4.8167 0 0 6 2 25.54 6.98 3.4878 1 0 1 6 26.10 100.00 3.4140 0 1 2 6 27.78 34.71 3.2111 0 0 9 2 28.24 82.57 3.1597 1 0 4 6 29.76 41.10 3.0023 0 1 5 6 33.49 26.69 2.6757 1 0 7 6 35.65 2.68 2.5187 0 1 8 6 37.34 2.81 2.4083 0 0 12 2 40.41 4.41 2.2320 1 0 10 6 42.99 20.08 2.1041 0 1 11 6 44.67 37.51 2.0285 1 1 0 6 45.71 3.35 1.9850 1 1 3 12 47.17 2.25 1.9267 0 0 15 2 48.46 18.90 1.8786 1 0 13 6 48.71 5.57 1.8695 1 1 6 12 51.33 12.36 1.7798 0 1 14 6 52.47 12.37 1.7439 2 0 2 6 53.43 30.36 1.7150 1 1 9 12 53.70 11.74 1.7070 0 2 4 6 54.60 7.01 1.6808 2 0 5 6 56.97 5.51 1.6165 0 2 7 6 57.36 6.63 1.6064 1 0 16 6 57.39 3.86 1.6056 0 0 18 2 59.59 3.43 1.5515 1 1 12 12 60.50 2.07 1.5303 0 1 17 6 63.73 5.40 1.4604 2 0 11 6 66.99 3.84 1.3970 1 1 15 12 68.02 5.73 1.3783 0 2 13 6 70.37 4.03 1.3379 2 0 14 6 70.46 3.01 1.3364 0 1 20 6 71.32 8.28 1.3224 1 2 2 12 72.35 8.16 1.3061 2 1 4 12 73.12 5.25 1.2942 1 2 5 12 75.15 4.35 1.2642 2 1 7 12 75.49 2.55 1.2593 0 2 16 6 75.52 8.98 1.2589 1 1 18 12 77.59 2.72 1.2304 1 0 22 6 81.15 4.71 1.1852 1 2 11 12 81.32 2.23 1.1831 0 1 23 6 82.33 4.47 1.1712 3 0 0 6 85.10 5.37 1.1400 2 1 13 12 87.30 3.97 1.1168 1 2 14 12 87.39 1.54 1.1160 2 0 20 6 88.96 2.79 1.1003 0 3 9 6 88.96 2.79 1.1003 3 0 9 6 89.18 1.78 1.0981 1 0 25 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.