Ba2 Cu3 O6.98 Pr Amador U, Moran E, Alario-Franco M, Ibanez J, Martin J, Rey T Solid State Ionics 63 (1993) 858-865 On the oxidation-reduction of Ba2PrCu3Oy single crystals _cod_database_code 1008639 _database_code_amcsd 0016528 CELL PARAMETERS: 3.8918 3.8918 11.6484 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 176.428 Density (g/cm3): 6.756 MAX. ABS. INTENSITY / VOLUME**2: 114.0873511 RIR: 5.498 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.59 14.66 11.6484 0 0 1 2 22.85 100.00 3.8918 1 0 0 4 22.90 7.20 3.8828 0 0 3 2 24.11 80.30 3.6912 1 0 1 8 27.57 83.26 3.2359 1 0 2 8 32.54 89.87 2.7519 1 1 0 4 32.58 2.42 2.7487 1 0 3 8 38.61 17.24 2.3316 1 0 4 8 38.65 4.19 2.3297 0 0 5 2 40.16 23.43 2.2452 1 1 3 8 45.34 2.13 2.0001 1 1 4 8 45.37 41.48 1.9989 1 0 5 8 46.68 48.89 1.9459 2 0 0 4 46.79 16.09 1.9414 0 0 6 2 51.39 2.09 1.7781 1 1 5 8 52.58 16.75 1.7405 2 1 0 8 52.61 2.54 1.7397 2 0 3 8 52.69 9.52 1.7372 1 0 6 8 53.21 14.51 1.7214 2 1 1 16 55.07 19.13 1.6676 2 1 2 16 55.20 2.20 1.6641 0 0 7 2 58.08 1.00 1.5882 2 1 3 16 58.15 24.09 1.5864 1 1 6 8 62.13 6.67 1.4940 2 1 4 16 62.15 3.10 1.4935 2 0 5 8 65.56 2.70 1.4240 1 1 7 8 67.13 20.85 1.3943 2 1 5 16 68.15 12.31 1.3760 2 2 0 4 68.24 16.49 1.3744 2 0 6 8 68.85 3.69 1.3637 1 0 8 8 72.92 2.56 1.2973 3 0 0 4 73.01 5.81 1.2959 2 1 6 16 73.44 2.24 1.2893 3 0 1 8 75.01 3.12 1.2662 3 0 2 8 75.12 2.87 1.2647 2 0 7 8 77.57 10.45 1.2307 3 1 0 8 81.17 1.28 1.1850 3 0 4 8 81.19 1.16 1.1847 2 2 5 8 82.16 3.20 1.1732 3 1 3 16 85.72 4.55 1.1334 3 0 5 8 86.74 7.27 1.1226 2 2 6 8 87.31 3.35 1.1168 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.