Co3Se4 Garcia-Garcia F J, Larsson A K, Noren L, Withers R L Solid State Sciences 6 (2004) 725-733 The crystal structures of Co3Se4 and Co7Se8 Note: single crystal _database_code_amcsd 0015522 CELL PARAMETERS: 12.1000 3.5700 6.1830 90.000 120.730 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 229.584 Density (g/cm3): 7.125 MAX. ABS. INTENSITY / VOLUME**2: 169.2612523 RIR: 7.735 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.68 4.88 5.3148 -2 0 1 2 16.68 2.37 5.3148 0 0 1 2 17.05 5.93 5.2005 2 0 0 2 26.40 3.39 3.3766 1 1 0 4 29.54 2.03 3.0240 -4 0 1 2 29.54 1.02 3.0240 2 0 1 2 33.73 19.17 2.6575 -3 1 1 4 33.73 44.54 2.6575 1 1 1 4 33.73 24.78 2.6574 -4 0 2 2 33.73 11.50 2.6574 0 0 2 2 34.49 3.41 2.6002 4 0 0 2 36.11 4.63 2.4872 3 1 0 4 39.52 2.00 2.2802 -3 1 2 4 45.59 19.35 1.9900 -5 1 1 4 45.59 21.46 1.9900 3 1 1 4 45.59 10.04 1.9899 -6 0 2 2 45.59 7.52 1.9899 2 0 2 2 46.88 2.77 1.9379 1 1 2 4 51.17 15.03 1.7850 0 2 0 2 51.18 28.87 1.7849 -3 1 3 4 51.59 1.53 1.7716 0 0 3 2 61.31 7.17 1.5120 -7 1 1 4 61.31 2.78 1.5120 5 1 1 4 61.31 1.42 1.5120 -8 0 2 2 61.31 3.32 1.5120 4 0 2 2 62.70 7.02 1.4818 -4 2 2 4 62.70 3.39 1.4818 0 2 2 4 62.70 1.35 1.4817 -6 0 4 2 62.70 2.48 1.4817 -2 0 4 2 63.18 1.17 1.4716 4 2 0 4 63.19 1.15 1.4716 -7 1 3 4 63.19 1.42 1.4716 1 1 3 4 64.50 1.39 1.4447 6 0 1 2 70.93 4.45 1.3288 -6 2 2 4 70.93 3.32 1.3288 2 2 2 4 70.93 2.44 1.3287 -8 0 4 2 70.93 2.32 1.3287 0 0 4 2 72.73 3.90 1.3001 8 0 0 2 83.86 2.44 1.1537 4 2 2 4 85.09 1.13 1.1401 -3 3 1 4 85.09 2.38 1.1401 1 3 1 4 85.09 1.07 1.1401 -6 2 4 4 85.09 1.89 1.1401 -2 2 4 4 86.71 1.06 1.1230 6 2 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.