Senarmontite Zav'yalova A A, Imamov R M Soviet Journal of Coordination Chemistry 1 (1975) 1186-1188 About the structure of the cubic modification of Sb2O3 Locality: synthetic Note: y(O) and z(O) corrected _database_code_amcsd 0015530 CELL PARAMETERS: 11.1000 11.1000 11.1000 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1367.631 Density (g/cm3): 5.662 MAX. ABS. INTENSITY / VOLUME**2: 238.2603080 RIR: 13.701 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.82 12.90 6.4086 1 1 1 8 27.84 100.00 3.2043 2 2 2 8 32.26 34.91 2.7750 4 0 0 6 35.24 7.78 2.5465 3 3 1 24 39.78 1.21 2.2658 4 2 2 24 42.31 1.82 2.1362 5 1 1 24 46.27 36.73 1.9622 4 4 0 12 48.52 1.45 1.8762 5 3 1 48 54.86 33.24 1.6734 6 2 2 24 57.52 8.65 1.6021 4 4 4 8 59.47 5.08 1.5543 5 5 1 24 64.48 2.18 1.4451 7 3 1 48 67.51 4.12 1.3875 8 0 0 6 69.29 3.70 1.3561 7 3 3 24 74.53 9.93 1.2733 6 6 2 24 76.81 8.54 1.2410 8 4 0 24 78.51 1.34 1.2184 9 1 1 24 85.76 5.49 1.1329 8 4 4 24 87.43 1.20 1.1156 7 7 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.