Cymrite
Drits V A, Kashaev A A, Sokolova G V
Soviet Physics Crystallography 20 (1975) 171-175
Crystal structure of cymrite
Note: Y(O11) corrected
_database_code_amcsd 0015567
5.33 36.59999 7.67 90 90. 90 P2_1
atom      x      y      z occ
Ba1  -.0249 -.0015  .0083
Ba2   .5267  .1235  .0083
Ba3   .0292  .2485  .0083
Ba4   .5267  .3735 -.0083
Al1    .506  .0416   .280  .5
Si1    .506  .0416   .280  .5
Al2    .510  .0416  -.270  .5
Si2    .510  .0416  -.270  .5
Al3   .0092   .083   .304  .5
Si3   .0092   .083   .304  .5
Al4   .0204   .083  -.265  .5
Si4   .0204   .083  -.265  .5
Al5   .0292   .167   .302  .5
Si5   .0292   .167   .302  .5
Al6   .0283   .167  -.268  .5
Si6   .0283   .167  -.268  .5
Al7    .529   .208   .302  .5
Si7    .529   .208   .302  .5
Al8    .527   .208  -.260  .5
Si8    .527   .208  -.260  .5
Al9    .535   .292   .292  .5
Si9    .535   .292   .292  .5
Al10   .528   .292  -.265  .5
Si10   .528   .292  -.265  .5
Al11  .0308   .333   .302  .5
Si11  .0308   .333   .302  .5
Al12  .0308   .333  -.260  .5
Si12  .0308   .333  -.260  .5
Al13  .0304   .417   .300  .5
Si13  .0304   .417   .300  .5
Al14  .0204   .417  -.265  .5
Si14  .0204   .417  -.265  .5
Al15   .521   .458   .302  .5
Si15   .521   .458   .302  .5
Al16   .521   .458  -.267  .5
Si16   .521   .458  -.267  .5
O1     .516  .0416   .506
O2    .0158  .0835   .522
O3    .0375   .167   .514
O4     .525   .210   .516
O5     .536   .290   .516
O6    .0258   .333   .516
O7    .0204   .416   .520
O8     .510   .458   .516
O9     .474   .000   .194
O10    .544 -.0006  -.222
O11    .294   .072   .218
O12    .218   .050  -.221
O13    .766   .062   .185
O14    .750   .064  -.171
O15  -.0416   .125   .225
O16    .036   .125  -.180
O17    .311   .178   .230
O18    .770   .186  -.180
O19    .811   .196   .230
O20    .270   .189  -.180
O21    .453   .250   .230
O22    .527   .250  -.185
O23    .811   .304   .233
O24    .269   .311  -.174
O25    .324   .324   .240
O26    .770   .314  -.180
O27   -.047   .375   .230
O28    .025   .375  -.184
O29    .307   .431   .226
O30    .770   .436  -.180
O31    .805   .444   .225
O32    .267   .439  -.179
Wat1  -.025  -.002   .387  .5
Wat2   .527   .124   .387  .5
Wat3   .029   .248   .387  .5
Wat4   .527   .374  -.387  .5
Wat5  -.025   .006   .624  .5
Wat6   .527   .131   .624  .5
Wat7   .029   .256   .624  .5
Wat8   .527   .382  -.624  .5