Daubreelite Babaev G Y, Kocharov A G, Ptasevich K, Yamzin I I, Vinnik M A, Saksonov Y G, Alferov V A, Gordeev I V, Tret'yakov Y D Soviet Physics Crystallography 20 (1975) 336-339 Magnetic and neutron diffraction studies of the sulfo-spinels Cu.2Fe.8Cr2S4 and Fe1.2Cr1.8S4 Locality: synthetic _database_code_amcsd 0015568 CELL PARAMETERS: 9.9890 9.9890 9.9890 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 996.704 Density (g/cm3): 3.850 MAX. ABS. INTENSITY / VOLUME**2: 45.20001278 RIR: 3.823 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.36 15.94 5.7672 1 1 1 8 25.22 35.00 3.5316 2 2 0 12 29.66 100.00 3.0118 3 1 1 24 31.01 1.51 2.8836 2 2 2 8 35.96 53.22 2.4973 4 0 0 6 44.43 11.63 2.0390 4 2 2 24 47.28 46.41 1.9224 5 1 1 24 47.28 3.23 1.9224 3 3 3 8 51.77 87.87 1.7658 4 4 0 12 54.33 2.16 1.6884 5 3 1 48 58.43 3.87 1.5794 6 2 0 24 60.81 10.61 1.5233 5 3 3 24 64.65 8.81 1.4418 4 4 4 8 66.89 2.90 1.3987 5 5 1 24 70.56 6.41 1.3348 6 4 2 48 72.71 9.90 1.3005 5 5 3 24 72.71 4.28 1.3005 7 3 1 48 76.26 10.95 1.2486 8 0 0 6 78.35 1.02 1.2204 7 3 3 24 81.82 1.69 1.1772 8 2 2 24 81.82 1.48 1.1772 6 6 0 12 83.88 3.52 1.1534 5 5 5 8 83.88 6.52 1.1534 7 5 1 48 87.31 9.60 1.1168 8 4 0 24 89.35 1.25 1.0964 9 1 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.