Aktashite Nowacki W Soviet Physics Crystallography 27 (1982) 26-27 Isotypy in aktashite Cu6Hg3As4S12 and nowackiite Cu6Zn3As4S12 Locality: not given _database_code_amcsd 0018891 CELL PARAMETERS: 13.7300 13.7300 9.3290 90.000 90.000 120.000 SPACE GROUP: R3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1523.024 Density (g/cm3): 5.453 MAX. ABS. INTENSITY / VOLUME**2: 207.1572096 RIR: 12.369 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.06 3.03 7.3396 1 0 1 3 12.90 11.21 6.8650 1 1 0 3 17.69 10.51 5.0137 0 2 1 3 20.45 2.37 4.3423 0 1 2 3 21.95 3.91 4.0489 2 1 1 3 24.25 3.67 3.6698 2 0 2 3 27.56 3.15 3.2364 -1 3 2 3 28.71 25.13 3.1097 0 0 3 1 28.71 2.67 3.1093 -1 4 1 3 28.71 72.20 3.1093 1 3 1 3 31.59 2.87 2.8326 1 1 3 3 31.59 1.13 2.8326 2 -1 3 3 33.27 21.70 2.6928 4 -1 2 3 33.27 1.13 2.6928 3 1 2 3 34.25 1.47 2.6182 3 2 1 3 34.57 4.09 2.5947 4 1 0 3 38.22 1.79 2.3548 -2 5 2 3 38.22 1.06 2.3548 2 3 2 3 39.38 2.75 2.2883 3 3 0 3 41.60 1.64 2.1712 0 2 4 3 42.68 1.31 2.1186 5 0 2 3 43.47 1.81 2.0818 6 -1 1 3 45.53 1.57 1.9923 -1 5 3 3 45.53 1.74 1.9923 4 1 3 3 47.52 1.39 1.9132 7 -3 1 3 47.76 22.47 1.9042 1 3 4 3 47.77 20.73 1.9040 5 2 0 3 49.45 1.24 1.8431 6 -3 3 3 56.68 8.01 1.6239 4 -1 5 3 56.69 7.45 1.6238 5 2 3 3 56.69 7.47 1.6238 -2 7 3 3 56.69 7.17 1.6238 8 -2 1 3 59.45 1.17 1.5548 0 0 6 1 59.46 3.12 1.5546 2 6 2 3 69.86 4.77 1.3464 8 -2 4 3 77.20 2.46 1.2356 1 3 7 3 77.21 2.19 1.2356 2 6 5 3 77.21 1.98 1.2355 -1 10 1 3 79.60 1.05 1.2043 -2 7 6 3 79.60 1.04 1.2043 5 2 6 3 89.05 2.23 1.0994 4 -1 8 3 89.06 1.73 1.0993 -1 10 4 3 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.