Ba2 Cu Hg O4.34 Pissas M, Billon B, Charalambous M, Chaussy J, LeFloch S, Bordet P, Capponi J Superconductivity: Science and Technology 10 (1997) 598-604 Single-crystal growth and characterization of the superconductor HgBa2CuO4+d _cod_database_code 1008819 _database_code_amcsd 0016688 CELL PARAMETERS: 3.8816 3.8816 9.5163 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 143.380 Density (g/cm3): 7.043 MAX. ABS. INTENSITY / VOLUME**2: 252.6322726 RIR: 11.680 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.65 1.66 4.7582 0 0 2 2 24.77 35.99 3.5941 1 0 1 8 28.13 12.05 3.1721 0 0 3 2 29.70 100.00 3.0077 1 0 2 8 32.62 56.27 2.7447 1 1 0 4 33.99 3.36 2.6372 1 1 1 8 36.58 2.99 2.4562 1 0 3 8 37.82 10.94 2.3791 0 0 4 2 43.61 20.93 2.0756 1 1 3 8 44.68 6.48 2.0284 1 0 4 8 46.81 23.39 1.9408 2 0 0 4 50.79 12.42 1.7977 1 1 4 8 53.63 14.13 1.7089 1 0 5 8 53.67 7.74 1.7077 2 1 1 16 55.51 6.67 1.6555 2 0 3 8 56.42 28.89 1.6308 2 1 2 16 58.16 2.25 1.5861 0 0 6 2 61.68 8.53 1.5039 2 0 4 8 63.35 1.80 1.4682 1 0 6 8 66.70 3.47 1.4023 2 1 4 16 68.30 3.84 1.3733 1 1 6 8 68.35 6.16 1.3724 2 2 0 4 73.89 9.25 1.2826 2 1 5 16 73.93 1.33 1.2821 3 0 1 8 75.48 2.44 1.2595 2 2 3 8 76.26 5.20 1.2485 3 0 2 8 77.76 3.30 1.2281 2 0 6 8 77.81 6.62 1.2275 3 1 0 8 78.52 2.80 1.2182 1 1 7 8 80.86 3.35 1.1888 2 2 4 8 82.36 1.58 1.1709 2 1 6 16 84.67 4.57 1.1448 3 1 3 16 85.35 3.87 1.1373 1 0 8 8 87.63 1.55 1.1135 2 0 7 8 89.94 3.92 1.0908 3 1 4 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.