Ba2 Cu Hg O4.27 Pissas M, Billon B, Charalambous M, Chaussy J, LeFloch S, Bordet P, Capponi J Superconductivity: Science and Technology 10 (1997) 598-604 Single-crystal growth and characterization of the superconductor HgBa2CuO4+d _cod_database_code 1008820 _database_code_amcsd 0016689 CELL PARAMETERS: 3.8792 3.8792 9.5117 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 143.134 Density (g/cm3): 7.042 MAX. ABS. INTENSITY / VOLUME**2: 255.8291190 RIR: 11.829 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.66 1.56 4.7558 0 0 2 2 24.79 35.97 3.5920 1 0 1 8 28.14 11.64 3.1706 0 0 3 2 29.72 100.00 3.0060 1 0 2 8 32.65 55.41 2.7430 1 1 0 4 34.02 3.32 2.6356 1 1 1 8 36.60 2.88 2.4549 1 0 3 8 37.83 10.82 2.3779 0 0 4 2 43.63 20.34 2.0744 1 1 3 8 44.70 6.25 2.0273 1 0 4 8 46.84 23.04 1.9396 2 0 0 4 50.82 12.30 1.7968 1 1 4 8 53.66 14.08 1.7080 1 0 5 8 53.71 7.71 1.7067 2 1 1 16 55.54 6.47 1.6546 2 0 3 8 56.46 28.82 1.6298 2 1 2 16 58.20 2.20 1.5853 0 0 6 2 61.72 8.45 1.5030 2 0 4 8 63.38 1.90 1.4675 1 0 6 8 66.74 3.35 1.4015 2 1 4 16 68.34 3.74 1.3725 1 1 6 8 68.40 6.07 1.3715 2 2 0 4 73.94 9.20 1.2818 2 1 5 16 73.98 1.33 1.2813 3 0 1 8 75.53 2.37 1.2588 2 2 3 8 76.32 5.18 1.2478 3 0 2 8 77.81 3.22 1.2275 2 0 6 8 77.87 6.53 1.2267 3 1 0 8 78.56 2.79 1.2176 1 1 7 8 80.92 3.32 1.1881 2 2 4 8 82.41 1.66 1.1703 2 1 6 16 84.73 4.45 1.1441 3 1 3 16 85.40 3.76 1.1368 1 0 8 8 87.69 1.55 1.1129 2 0 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.