Ba2 Cu Hg O4.01 Pissas M, Billon B, Charalambous M, Chaussy J, LeFloch S, Bordet P, Capponi J Superconductivity: Science and Technology 10 (1997) 598-604 Single-crystal growth and characterization of the superconductor HgBa2CuO4+d _cod_database_code 1008821 _database_code_amcsd 0016690 CELL PARAMETERS: 3.8776 3.8776 9.5005 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 142.847 Density (g/cm3): 7.008 MAX. ABS. INTENSITY / VOLUME**2: 261.3921054 RIR: 12.145 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.68 1.33 4.7502 0 0 2 2 24.80 37.07 3.5901 1 0 1 8 28.18 11.05 3.1668 0 0 3 2 29.74 100.00 3.0039 1 0 2 8 32.66 53.49 2.7419 1 1 0 4 34.03 2.96 2.6344 1 1 1 8 36.64 2.64 2.4528 1 0 3 8 37.88 10.28 2.3751 0 0 4 2 43.67 19.50 2.0729 1 1 3 8 44.75 6.40 2.0254 1 0 4 8 46.86 22.31 1.9388 2 0 0 4 50.86 11.67 1.7952 1 1 4 8 53.72 14.06 1.7063 1 0 5 8 53.73 7.86 1.7059 2 1 1 16 55.58 6.20 1.6535 2 0 3 8 56.49 28.69 1.6290 2 1 2 16 58.27 2.14 1.5834 0 0 6 2 61.77 8.07 1.5019 2 0 4 8 63.46 1.90 1.4659 1 0 6 8 66.79 3.41 1.4005 2 1 4 16 68.42 3.65 1.3712 1 1 6 8 68.43 5.88 1.3709 2 2 0 4 74.01 9.17 1.2809 2 1 5 16 74.02 1.34 1.2807 3 0 1 8 75.58 2.28 1.2581 2 2 3 8 76.36 5.15 1.2472 3 0 2 8 77.90 3.15 1.2264 2 0 6 8 77.91 6.33 1.2262 3 1 0 8 78.66 2.67 1.2164 1 1 7 8 80.97 3.18 1.1873 2 2 4 8 82.49 1.66 1.1693 2 1 6 16 84.78 4.30 1.1435 3 1 3 16 85.52 3.73 1.1355 1 0 8 8 87.79 1.48 1.1119 2 0 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.