Ba2 Cu Hg O4.24 Pissas M, Billon B, Charalambous M, Chaussy J, LeFloch S, Bordet P, Capponi J Superconductivity: Science and Technology 10 (1997) 598-604 Single-crystal growth and characterization of the superconductor HgBa2CuO4+d _cod_database_code 1008823 _database_code_amcsd 0016692 CELL PARAMETERS: 3.8751 3.8751 9.4852 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 142.434 Density (g/cm3): 7.071 MAX. ABS. INTENSITY / VOLUME**2: 260.4835591 RIR: 11.995 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.71 1.50 4.7426 0 0 2 2 24.82 35.74 3.5873 1 0 1 8 28.23 11.06 3.1617 0 0 3 2 29.77 100.00 3.0008 1 0 2 8 32.68 54.69 2.7401 1 1 0 4 34.06 3.38 2.6325 1 1 1 8 36.68 2.82 2.4498 1 0 3 8 37.94 10.65 2.3713 0 0 4 2 43.72 19.53 2.0707 1 1 3 8 44.81 5.73 2.0226 1 0 4 8 46.89 22.74 1.9375 2 0 0 4 50.93 12.16 1.7931 1 1 4 8 53.77 7.63 1.7048 2 1 1 16 53.80 13.94 1.7038 1 0 5 8 55.63 6.20 1.6520 2 0 3 8 56.54 28.77 1.6277 2 1 2 16 58.37 2.14 1.5809 0 0 6 2 61.84 8.36 1.5004 2 0 4 8 63.56 2.09 1.4637 1 0 6 8 66.87 3.10 1.3992 2 1 4 16 68.48 5.98 1.3701 2 2 0 4 68.53 3.63 1.3693 1 1 6 8 74.07 1.31 1.2799 3 0 1 8 74.10 9.12 1.2795 2 1 5 16 75.65 2.27 1.2571 2 2 3 8 76.42 5.17 1.2463 3 0 2 8 77.97 6.44 1.2254 3 1 0 8 78.01 3.13 1.2249 2 0 6 8 78.79 2.82 1.2146 1 1 7 8 81.06 3.30 1.1863 2 2 4 8 82.61 1.82 1.1679 2 1 6 16 84.86 4.30 1.1426 3 1 3 16 85.68 3.53 1.1338 1 0 8 8 87.94 1.57 1.1104 2 0 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.