Behoite
      Jacobs H, Niemann A, Kockelmann W
      Zeitschrift fur Anorganische und Allgemeine Chemie 631 (2005) 1247-1254
      Low temperature investigations of hydrogen bridge bonds in the hydroxides
      beta-Be(OH)2 and epsilon-Zn(OH)2 by Raman-spectroscopy as well as X-ray and neutron diffraction
      Locality: synthetic
      Sample: T = 245 K
      _database_code_amcsd 0015821

      CELL PARAMETERS:    4.5356   4.6317   7.0379   90.000   90.000   90.000
      SPACE GROUP: P2_12_12_1
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    147.849
      Density (g/cm3):      1.933
      MAX. ABS. INTENSITY / VOLUME**2:      5.202302367    
      RIR:      0.876
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                22.99         68.79        3.8690    0   1   1         4
                23.33         51.67        3.8125    1   0   1         4
                30.37         24.74        2.9435    1   1   1         4
                31.94          1.09        2.8020    0   1   2         4
                32.20         26.86        2.7803    1   0   2         4
                37.74        100.00        2.3838    1   1   2         4
                38.89          2.33        2.3159    0   2   0         2
                39.75          7.66        2.2678    2   0   0         2
                41.03         18.62        2.1998    0   2   1         4
                41.85          2.99        2.1585    2   0   1         4
                43.23          1.56        2.0928    0   1   3         4
                43.43          3.52        2.0837    1   0   3         4
                44.48          6.58        2.0368    2   1   0         4
                45.85         17.64        1.9793    1   2   1         4
                46.41         18.71        1.9565    2   1   1         4
                46.97          1.05        1.9345    0   2   2         4
                47.87         13.90        1.9003    1   1   3         4
                51.35          8.04        1.7794    1   2   2         4
                51.87          1.78        1.7628    2   1   2         4
                51.97          3.35        1.7595    0   0   4         2
                55.90          6.11        1.6448    0   1   4         4
                56.06          1.15        1.6404    1   0   4         4
                56.43          4.27        1.6305    2   0   3         4
                56.82          2.25        1.6203    2   2   0         4
                58.45          3.67        1.5790    2   2   1         4
                59.69          3.23        1.5490    1   2   3         4
                60.17          3.72        1.5380    2   1   3         4
                64.88          1.07        1.4372    3   1   0         4
                65.19          3.13        1.4310    1   3   1         4
                66.39          2.24        1.4082    3   1   1         4
                66.77          1.98        1.4010    0   2   4         4
                67.36          2.65        1.3901    2   0   4         4
                69.66          1.93        1.3498    1   3   2         4
                70.76          3.54        1.3315    2   1   4         4
                70.82          2.17        1.3305    3   1   2         4
                73.42          2.02        1.2897    0   3   3         4
                74.32          3.43        1.2762    2   3   0         4
                74.69          4.30        1.2708    3   0   3         4
                75.75          1.59        1.2557    2   3   1         4
                76.45          1.59        1.2460    3   2   1         4
                76.85          3.99        1.2405    1   3   3         4
                79.72          3.27        1.2028    0   2   5         4
                80.60          1.80        1.1919    2   2   4         4
                80.66          4.57        1.1912    3   2   2         4
                83.07          1.12        1.1626    1   2   5         4
                83.48          2.12        1.1580    2   1   5         4
                84.87          1.35        1.1426    0   4   1         4
                85.51          1.43        1.1356    1   0   6         4
                88.69          1.48        1.1030    1   1   6         4
                88.85          1.13        1.1014    4   1   0         4
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.