Behoite
      Jacobs H, Niemann A, Kockelmann W
      Zeitschrift fur Anorganische und Allgemeine Chemie 631 (2005) 1247-1254
      Low temperature investigations of hydrogen bridge bonds in the hydroxides
      beta-Be(OH)2 and epsilon-Zn(OH)2 by Raman-spectroscopy as well as X-ray and neutron diffraction
      Locality: synthetic
      Sample: T = 5 K
      _database_code_amcsd 0015823

      CELL PARAMETERS:    4.5259   4.6314   7.0193   90.000   90.000   90.000
      SPACE GROUP: P2_12_12_1
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    147.133
      Density (g/cm3):      1.942
      MAX. ABS. INTENSITY / VOLUME**2:      4.861847314    
      RIR:      0.815
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                23.01         71.63        3.8657    0   1   1         4
                23.39         55.68        3.8038    1   0   1         4
                25.38          1.13        3.5096    0   0   2         2
                30.41         28.72        2.9395    1   1   1         4
                32.00          1.14        2.7972    0   1   2         4
                32.28         32.19        2.7735    1   0   2         4
                37.81        100.00        2.3794    1   1   2         4
                38.89          2.08        2.3157    0   2   0         2
                39.84          7.10        2.2629    2   0   0         2
                41.04         20.73        2.1991    0   2   1         4
                41.95          3.21        2.1538    2   0   1         4
                43.33          1.64        2.0884    0   1   3         4
                43.54          4.13        2.0784    1   0   3         4
                44.56          7.36        2.0332    2   1   0         4
                45.88         18.60        1.9780    1   2   1         4
                46.50         20.21        1.9529    2   1   1         4
                47.83          1.02        1.9019    2   0   2         4
                47.98         15.49        1.8963    1   1   3         4
                51.40          8.96        1.7776    1   2   2         4
                51.98          2.02        1.7593    2   1   2         4
                52.12          2.85        1.7548    0   0   4         2
                56.04          7.06        1.6410    0   1   4         4
                56.22          1.14        1.6361    1   0   4         4
                56.58          4.95        1.6266    2   0   3         4
                56.89          2.14        1.6185    2   2   0         4
                58.53          3.81        1.5771    2   2   1         4
                59.79          2.98        1.5468    1   2   3         4
                60.31          3.53        1.5347    2   1   3         4
                65.02          1.15        1.4344    3   1   0         4
                65.22          3.22        1.4305    1   3   1         4
                66.53          2.48        1.4054    3   1   1         4
                66.90          1.82        1.3986    0   2   4         4
                67.55          2.36        1.3867    2   0   4         4
                69.71          2.28        1.3489    1   3   2         4
                70.47          1.01        1.3363    1   2   4         4
                70.94          3.70        1.3285    2   1   4         4
                70.98          2.40        1.3278    3   1   2         4
                73.49          2.13        1.2886    0   3   3         4
                74.39          3.71        1.2753    2   3   0         4
                74.89          4.46        1.2679    3   0   3         4
                75.82          1.66        1.2548    2   3   1         4
                76.59          1.39        1.2440    3   2   1         4
                76.93          4.07        1.2393    1   3   3         4
                79.91          3.42        1.2005    0   2   5         4
                80.78          2.22        1.1897    2   2   4         4
                80.82          4.73        1.1893    3   2   2         4
                83.27          1.10        1.1604    1   2   5         4
                83.72          2.04        1.1552    2   1   5         4
                84.88          1.34        1.1424    0   4   1         4
                85.79          1.46        1.1327    1   0   6         4
                88.96          1.54        1.1002    1   1   6         4
                89.08          1.23        1.0991    4   1   0         4
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs