K2 Te Zintl E, Harder A, Dauth B Zeitschrift fur Elektrochemie 40 (1934) 588-593 Gitterstruktur der Oxide, Sulfide, Selenide und Telluride des Lithiums, Natriums und Kaliums _cod_database_code 1011377 _database_code_amcsd 0018211 CELL PARAMETERS: 8.1520 8.1520 8.1520 90.000 90.000 90.000 SPACE GROUP: Fm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 541.742 Density (g/cm3): 2.523 MAX. ABS. INTENSITY / VOLUME**2: 80.17699799 RIR: 10.348 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.85 86.93 4.7066 1 1 1 8 21.80 4.60 4.0760 2 0 0 6 31.03 100.00 2.8822 2 2 0 12 36.56 45.38 2.4579 3 1 1 24 38.25 1.73 2.3533 2 2 2 8 44.45 16.38 2.0380 4 0 0 6 48.69 18.71 1.8702 3 3 1 24 50.04 2.76 1.8228 4 2 0 24 55.20 30.87 1.6640 4 2 2 24 58.86 3.31 1.5689 3 3 3 8 58.86 9.92 1.5689 5 1 1 24 64.68 8.67 1.4411 4 4 0 12 68.04 12.05 1.3779 5 3 1 48 69.14 1.18 1.3587 4 4 2 24 73.47 10.98 1.2889 6 2 0 24 76.65 4.05 1.2432 5 3 3 24 81.87 2.55 1.1766 4 4 4 8 84.96 2.97 1.1415 7 1 1 24 84.96 2.97 1.1415 5 5 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.