delta-AlOOD
      Furukawa A S, Komatsu K, Vanpeteghem C B, Ohtani E
      American Mineralogist 93 (2008) 1558-1567
      Neutron diffraction study of delta-AlOOD at high pressure and its implication
      for symmetrization of the hydrogen bond
      Note: P = 7. 9 GPa
      Locality: synthetic
      _database_code_amcsd 0004669

      CELL PARAMETERS:    4.6432   4.1529   2.8000   90.000   90.000   90.000
      SPACE GROUP: P2_1nm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     53.992
      Density (g/cm3):      3.674
      MAX. ABS. INTENSITY / VOLUME**2:      13.14592921    
      RIR:      1.165
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                21.40          1.15        4.1529    0   1   0         2
                28.84        100.00        3.0954    1   1   0         2
                37.51          3.81        2.3978    1   0   1         2
                38.79         57.39        2.3216    0   1   1         4
                38.79         10.43        2.3216    2   0   0         1
                43.59         63.97        2.0765    1   1   1         4
                44.72         37.89        2.0264    2   1   0         2
                48.00          1.43        1.8955    1   2   0         2
                56.02         32.81        1.6416    2   1   1         4
                58.83         66.09        1.5697    1   2   1         4
                59.75         23.02        1.5477    2   2   0         2
                64.22         10.70        1.4503    3   1   0         2
                66.82         17.71        1.4000    0   0   2         2
                69.38         28.63        1.3546    3   0   1         2
                71.06          7.50        1.3266    1   3   0         2
                73.54          1.14        1.2878    3   1   1         4
                74.37         12.25        1.2756    1   1   2         4
                76.81          4.49        1.2409    0   3   1         4
                80.04          2.82        1.1989    2   0   2         2
                80.04          6.15        1.1989    1   3   1         4
                80.84          4.09        1.1890    2   3   0         2
                84.02          6.00        1.1518    2   1   2         4
                87.19          1.26        1.1179    4   1   0         2
                89.57          7.70        1.0944    2   3   1         4
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs