Phillipsite Gatta G D, Cappelletti P, Rotiroti N, Slebodnick C, Rinaldi R American Mineralogist 94 (2009) 190-199 New insights into the crystal structure and crystal chemistry of the zeolite phillipsite Locality: "Newer Volcanic Suite," Richmond, Melbourne, Victoria, Australia Note: T = 298 K Note: Chemistry and structural occupancy are not consistent _database_code_amcsd 0004834 9.9238 14.3145 8.7416 90 124.920 90 P2_1/m atom x y z occ Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) K1 .8674 .25 .226 .58 .0543 .078 .023 .065 0 .042 0 K2 .8451 .25 .187 .30 .059 .057 .035 .112 0 .064 0 Na .6682 .37452 .5593 .36 .0324 .0334 .0416 .0267 -.0131 .0199 -.0075 Ca .6682 .37452 .5593 .16 .0324 .0334 .0416 .0267 -.0131 .0199 -.0075 Al1 .72527 .00683 .28477 .375 .01380 .0123 .0156 .0122 .0007 .0063 -.0008 Al2 .42172 .13923 .04494 .375 .01350 .0122 .0122 .0145 .0010 .0067 -.0003 Al3 .04307 .02522 .28043 .375 .01287 .0142 .0139 .0112 -.0017 .0077 -.0009 Al4 .08288 .14052 .00296 .375 .01359 .0166 .0112 .0156 -.0009 .0108 -.0005 Si1 .72527 .00683 .28477 .625 .01380 .0123 .0156 .0122 .0007 .0063 -.0008 Si2 .42172 .13923 .04494 .625 .01350 .0122 .0122 .0145 .0010 .0067 -.0003 Si3 .04307 .02522 .28043 .625 .01287 .0142 .0139 .0112 -.0017 .0077 -.0009 Si4 .08288 .14052 .00296 .625 .01359 .0166 .0112 .0156 -.0009 .0108 -.0005 O1 .0615 .11290 .1724 .0250 .0347 .0237 .0235 -.0004 .0207 .0036 O2 .6291 .58688 .1499 .0261 .0326 .0239 .0221 .0050 .0158 .0056 O3 .5947 .09597 .2286 .0276 .0204 .0280 .0241 .0072 .0067 -.0010 O4 .0399 .92452 .1868 .0267 .0306 .0196 .0251 -.0006 .0130 -.0060 O5 .8771 .04490 .2722 .0262 .0247 .0282 .0331 -.0015 .0207 -.0008 O6 .2793 .37402 .0853 .0299 .0237 .0350 .0358 -.0020 .0197 -.0015 O7 .7927 .52202 .5036 .0249 .0211 .0333 .0152 .0012 .0074 -.0020 O8 .5455 .75 -.0257 .0275 .0360 .0148 .0336 0 .0211 0 O9 .0224 .25 -.0610 .0276 .0343 .0160 .0269 0 .0143 0 Wat1 1.2177 .25 .5627 .91 .081 .130 .042 .047 0 .036 0 Wat2 .2129 .75 .4774 .95 .088 .060 .127 .039 0 .007 0 Wat3 .3513 .6450 .1717 .87 .110 .070 .180 .095 .005 .055 -.006 Wat4 .582 .786 .568 .29 .066 .032 .093 .047 .003 .008 -.008 Wat4 .545 .735 .551 .14 .051 Wat5 .5209 .9854 .5421 .432 .084 .076 .116 .096 .009 .071 .042 Wat6 .5984 .8864 .5662 .30 .133 .075 .189 .058 -.070 -.008 .064