Magnetite
      Glazyrin K, McCammon C, Dubrovinsky L, Merlini M, Schollenbruch K, Woodland A,
      Hanfland M
      American Mineralogist 97 (2012) 128-133
      Effect of high pressure on the crystal structure and electronic properties
      of magnetite below 25 GPa
      Note: P = 2.9 GPa
      Locality: synthetic
      _database_code_amcsd 0020646

      CELL PARAMETERS:    8.3500   8.3500   8.3500   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    582.183
      Density (g/cm3):      5.282
      MAX. ABS. INTENSITY / VOLUME**2:      91.76823744    
      RIR:      5.657
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.40          8.52        4.8209    1   1   1         8
                30.27         28.35        2.9522    2   2   0        12
                35.66        100.00        2.5176    3   1   1        24
                37.30          8.48        2.4104    2   2   2         8
                43.35         19.93        2.0875    4   0   0         6
                53.78          9.23        1.7044    4   2   2        24
                57.34          6.06        1.6070    3   3   3         8
                57.34         24.49        1.6070    5   1   1        24
                62.97         39.78        1.4761    4   4   0        12
                71.45          3.26        1.3203    6   2   0        24
                74.52          8.26        1.2734    5   3   3        24
                75.53          3.89        1.2588    6   2   2        24
                79.53          2.47        1.2052    4   4   4         8
                87.40          3.53        1.1158    6   4   2        48
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.