Magnetite
      Glazyrin K, McCammon C, Dubrovinsky L, Merlini M, Schollenbruch K, Woodland A,
      Hanfland M
      American Mineralogist 97 (2012) 128-133
      Effect of high pressure on the crystal structure and electronic properties
      of magnetite below 25 GPa
      Note: P = 8.6 GPa
      Locality: synthetic
      _database_code_amcsd 0020649

      CELL PARAMETERS:    8.2720   8.2720   8.2720   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    566.020
      Density (g/cm3):      5.433
      MAX. ABS. INTENSITY / VOLUME**2:      94.29980612    
      RIR:      5.651
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.58          8.63        4.7758    1   1   1         8
                30.57         28.43        2.9246    2   2   0        12
                36.01        100.00        2.4941    3   1   1        24
                37.67          8.54        2.3879    2   2   2         8
                43.77         19.80        2.0680    4   0   0         6
                54.33          9.16        1.6885    4   2   2        24
                57.93          6.00        1.5919    3   3   3         8
                57.93         24.34        1.5919    5   1   1        24
                63.63         39.32        1.4623    4   4   0        12
                72.23          3.23        1.3079    6   2   0        24
                75.34          8.19        1.2615    5   3   3        24
                76.37          3.88        1.2471    6   2   2        24
                80.43          2.44        1.1940    4   4   4         8
                88.44          3.52        1.1054    6   4   2        48
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.