Magnetite
      Glazyrin K, McCammon C, Dubrovinsky L, Merlini M, Schollenbruch K, Woodland A,
      Hanfland M
      American Mineralogist 97 (2012) 128-133
      Effect of high pressure on the crystal structure and electronic properties
      of magnetite below 25 GPa
      Note: P = 19.1 GPa
      Locality: synthetic
      _database_code_amcsd 0020659

      CELL PARAMETERS:    8.1490   8.1490   8.1490   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    541.144
      Density (g/cm3):      5.683
      MAX. ABS. INTENSITY / VOLUME**2:      98.81464452    
      RIR:      5.662
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.86          8.30        4.7048    1   1   1         8
                31.04         28.36        2.8811    2   2   0        12
                36.57        100.00        2.4570    3   1   1        24
                38.26          8.57        2.3524    2   2   2         8
                44.47         19.57        2.0373    4   0   0         6
                55.22          9.05        1.6634    4   2   2        24
                58.89          6.05        1.5683    3   3   3         8
                58.89         23.57        1.5683    5   1   1        24
                64.71         38.57        1.4406    4   4   0        12
                73.50          3.19        1.2885    6   2   0        24
                76.68          8.06        1.2427    5   3   3        24
                77.74          3.82        1.2285    6   2   2        24
                81.90          2.40        1.1762    4   4   4         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.